Total Finathene® 1288 HDPE film (discontinued **)

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Total Finathene® 1288 HDPE film (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Applications: Flat bottom bags, draw strings, coextruded merchandise bags, deli wrapInformation provided provided by Total Petrochemicals.Total Petrochemicals includes former Fina and Atofina plastics product lines.

Physical Properties	Metric	English	Comments
Density	0.959 g/cc	0.0346 lb/in³	ASTM D 792
Water Vapor Transmission	6.20 g/m²/day	0.399 g/100 in²/day	100°F; E 96/66
Thickness	20.3 microns	0.800 mil
Melt Flow	0.070 g/10 min @Load 2.16 kg	0.070 g/10 min @Load 4.76 lb	ISO 1133
	0.35 g/10 min @Load 5.00 kg	0.35 g/10 min @Load 11.0 lb	ISO 1133
High Load Melt Index	9.5 g/10 min @Load 21.6 kg	9.5 g/10 min @Load 47.6 lb	ISO 1133

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	>= 42.7 MPa	>= 6200 psi	ASTM D 882 A
Film Tensile Strength at Yield, TD	>= 52.4 MPa	>= 7600 psi	ASTM D 882 A
Film Elongation at Break, MD	300 - 500 %	300 - 500 %	ASTM D 882 A
Film Elongation at Break, TD	300 - 500 %	300 - 500 %	ASTM D 882 A
Secant Modulus, MD	0.910 GPa	132 ksi	ASTM D 882 A
Secant Modulus, TD	1.00 GPa	145 ksi	ASTM D 882 A
Elmendorf Tear Strength MD	22 g	22 g	ASTM D 1922
Elmendorf Tear Strength TD	140 g	140 g	ASTM D 1922
Dart Drop Test	320 g	0.706 lb	ASTM D 1709
Film Tensile Strength at Break, MD	>= 68.9 MPa	>= 10000 psi	ASTM D 882 A
Film Tensile Strength at Break, TD	>= 63.8 MPa	>= 9250 psi	ASTM D 882 A

Thermal Properties	Metric	English	Comments
Melting Point	129 °C	265 °F	ASTM D3417