Techmer ES HiFill® PC GF30 X 30% Glass Filled
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 30% Glass Filled |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® PC GF30 X 30% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ASTM D792 |
| Water Absorption | 0.080 % @Time 86400 sec |
0.080 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm @Thickness 3.17 mm |
0.0010 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 114 MPa | 16500 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 159 MPa | 23000 psi | ASTM D790 |
| Flexural Modulus | 7.58 GPa | 1100 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 3.17 mm |
2.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 8.54 J/cm @Thickness 3.17 mm |
16.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 23.4 µm/m-°C | 13.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 305 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | 2.00 | 2.00 |
Users viewing this material also viewed the following:
- Murtfeldt Murlubric® [FS] Oil Modified Nylon 6
- Fainplast Compounds RE 925 Rigid PVC, Extrusion
- Fujipoly Industries Sarcon® GR-c Gap Filler Pad
- Gromax Standard GB9567-97
- SABIC Innovative Plastics Valox® 3706 PBT+PC
- Styrolution PS 576H HIPS
- Arkema Group Rilsan® AZM 23 T6LD Nylon 12, 23% Glass Fiber Filled (Conditioned)
- Akro-Plastic Akromid® A3 GF 30 (2397) PA 6.6 Dry, 30% Glass Filled
- Axiall 21571 Coax & Telecom Flexible PVC
- A. Schulman POLYBATCH™ Red 5557 Concentrate Based In Polyethylene
Copyright © lookpolymers.com All Rights Reserved