Stellar Canada CERAMITE® BKR-F Wear Resistant Castable

Category Ceramic , Oxide , Aluminum Oxide
Manufacturer Stellar Canada
Trade Name CERAMITE®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Stellar Canada CERAMITE® BKR-F Wear Resistant Castable.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ceramite is a family of wear resistant castables with a unique combination of high wear resistance, thermal resistance and mechanical strength. Ceramite is produced and supplied to end users world wide, both as mortars and as various precast components. Ceramite can easily be mixed, cast and shaped in any size and is thus comfortably to work with in-situ. Ceramite can be used in within a wide range of temperatures and applications exposed to thermal shock conditions in industries like for example aluminum, cement and ferro.Applications: Floor Tile, Hearth/Furnace Tile, Furnace Sills & Doors, Lintels, Pipe and Duct Linings, Feed Tubes, Troughs/Launders, Ladles, Dampers, Nozzle Blasters, Crucible Linings, Vortex, Burner Tip Cooler Plates, Nose Ring, Electrical Insulation, Cold Wear AreasSpecific Notes on This Grade: A trowelable formulation with good thermal and electrical insulating properties. A castable widely used in aluminum, ferro alloys, mining, cement, and steel industriesInformation provided by Stellar Canada.
Physical Properties Metric English Comments
Bulk Density 2.79 g/cc
0.101 lb/in³
Trowellable
Mechanical Properties Metric English Comments
Modulus of Rupture 0.02100 GPa
3.046 ksi
Hot, prefired at 1832°F/24 hours (1000°C)
Flexural Strength 9.011 MPa

@Temperature 1200 °C
1307 psi

@Temperature 2192 °F
after Firing; ASTM-349
16.50 MPa

@Temperature 850.0 °C
2393 psi

@Temperature 1562 °F
after Firing; ASTM-349
16.60 MPa

@Temperature 500 °C
2408 psi

@Temperature 932 °F
after Firing; ASTM-349
17.90 MPa

@Temperature 1000 °C
2596 psi

@Temperature 1832 °F
after Firing; ASTM-349
Compressive Strength 104.00 MPa

@Temperature 1200 °C
15084 psi

@Temperature 2190 °F
after Firing; ASTM C-349
121.0 MPa

@Temperature 1000 °C
17550 psi

@Temperature 1830 °F
after Firing; ASTM C-349
132.00 MPa

@Temperature 850 °C
19145 psi

@Temperature 1560 °F
after Firing; ASTM C-349
169.00 MPa

@Temperature 500 °C
24512 psi

@Temperature 932 °F
after Firing; ASTM C-349
180.00 MPa

@Temperature 20.0 °C
26107 psi

@Temperature 68.0 °F
after 7 days
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 1200 °C
2192 °F
Component Elements Properties Metric English Comments
Al2O3 76 %
76 %
CaO 7.0 %
7.0 %
Fe2O3 1.01 %
1.01 %
K2O 0.15 %
0.15 %
MgO 0.090 %
0.090 %
Na2O 0.070 %
0.070 %
SiO2 13 %
13 %
TiO2 2.0 %
2.0 %
Descriptive Properties Value Comments
Application Troweling