- Solvay Specialty Polymers Solef® 20808 Polyvinylidene Fluoride (PVDF)
Solvay Specialty Polymers Solef® 20808 Polyvinylidene Fluoride (PVDF)
| Category | Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Solef® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Solef® 20808 Polyvinylidene Fluoride (PVDF).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Copolymer; Low ViscosityAdditional Properties: Abrasion Resistance - ASTM D4060 29.0 mg; Coefficient of Friction - ASTM D1894 0.280; Coefficient of Linear Thermal Expansion - ASTM D696 1.4E-4 to 1.6E-4 cm/cm/°C; Crystallization Heat - ASTM D3417 35.0 J/g; Crystallization Point - ASTM D3418 120 °C; Density - ISO 1183 1.783 g/cm³; Dielectric Constant - ASTM D150 6.80; Flammability - UL 94 V-0; Glass Transition Temperature - ASTM D4065 -50.0 °C; Hardness - ASTM D2240 (2.00 mm): 71.0; Heat of Fusion - ASTM D3418 35.0 J/g; Izod Impact - ASTM D256 86.0 J/m; Thermal Stability - 410 °CInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Absorption | <= 0.040 % @Time 86400 sec |
<= 0.040 % @Time 24.0 hour |
ISO 62 |
| Melt Flow | 5.4 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.4 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 56.0 MPa | 8120 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 33.0 MPa | 4790 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 600 % | 600 % | ASTM D638 |
| Elongation at Yield | 10 % | 10 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 1.08 GPa | 157 ksi | 1.0 mm/min; ASTM D638 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 1.20 J/g-°C @Temperature 23.0 °C |
0.287 BTU/lb-°F @Temperature 73.4 °F |
ASTM C351 |
| 1.60 J/g-°C @Temperature 100 °C |
0.382 BTU/lb-°F @Temperature 212 °F |
ASTM C351 | |
| Thermal Conductivity | 0.200 W/m-K @Temperature 23.0 °C |
1.39 BTU-in/hr-ft²-°F @Temperature 73.4 °F |
ASTM C177 |
| Melting Point | 148 °C | 298 °F | DSC |
| Oxygen Index | 44 % @Thickness 3.00 mm |
44 % @Thickness 0.118 in |
ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | ASTM D257 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 141R PC
- Ferro EG 0221 Specialty Glass
- Flint Hills P4G2Z-159 Polypropylene Homopolymer
- Taiwan PU Corporation PPG CPU-2079 Polyurethane Casting Elastomer
- Solvay Chemicals Allyl chloride High purity – Non stabilized 3-chloropropene
- A. Schulman POLYBATCH™ Yellow P20199/2 Concentrate Based In Copolymer PP
- Diamond Polymers ASA TW-15H
- Axiall PURGOVIN® 8000 Rigid PVC, Extrusion
- BASF Elastollan® 1190A Polyether Type Polyurethane Elastomer
- Braskem FF650WV Homopolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved