- HOME
- POLYMER SEARCH
- Thermoplastic
- Polyphenylene Sulfide (PPS)
- Polyphenylene Sulfide (PPS) with 40% Glass Fiber Filler
- Sichuan Deyang Haton® hGR40DL Polyphenylene Sulfide, Glass Fiber Reinforced
Sichuan Deyang Haton® hGR40DL Polyphenylene Sulfide, Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 40% Glass Fiber Filler |
| Manufacturer | Sichuan Deyang Chemical Co. Ltd. |
| Trade Name | Haton® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sichuan Deyang Haton® hGR40DL Polyphenylene Sulfide, Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Injection molding, low chlorineInformation provided by Sichuan Deyang Chemical Co., LTD
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in³ | GB/T 1033.1-2008 |
| Water Absorption | 0.020 % | 0.020 % | GB/T 1034-2008 |
| Linear Mold Shrinkage, Flow | 0.0025 cm/cm | 0.0025 in/in | GB/T 15585-1995 |
| Linear Mold Shrinkage, Transverse | 0.0075 cm/cm | 0.0075 in/in | GB/T 15585-1995 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 108 | 108 | GB/T 3398.2-2008 |
| Tensile Strength | 180 MPa | 26100 psi | GB/T 1040.2-2006 |
| Elongation at Break | 1.4 % | 1.4 % | GB/T1040.2-2006 |
| Flexural Strength | 265 MPa | 38400 psi | GB/T 9341-2008 |
| Flexural Modulus | 14.9 GPa | 2160 ksi | GB/T 9341-2008 |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² | 7.61 ft-lb/in² | GB/T 1843-2008 |
| Izod Impact, Unnotched (ISO) | 46.0 kJ/m² | 21.9 ft-lb/in² | GB/T 1843-2008 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 280 °C | 536 °F | GBT/T 19466.3-2004 |
| Deflection Temperature at 1.8 MPa (264 psi) | 268 °C | 514 °F | GB/T 1634.2-2004 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 3.30e+16 ohm-cm | 3.30e+16 ohm-cm | GB/T1410-2006 |
| Surface Resistivity per Square | 7.00e+15 ohm | 7.00e+15 ohm | GB/T1410-2006 |
| Dielectric Constant | 4.0 | 4.0 | GB/T 1409-2006 |
| Dielectric Strength | 16.0 kV/mm | 406 kV/in | GB/T1408.1-2006 |
| Dissipation Factor | 0.0020 | 0.0020 | GB/T 1409-2006 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering S65T Silicone Rubber
- SABIC Innovative Plastics GELOY CR7020 ASA (Asia Pacific)
- Ineos Nova Zylar® 221 Clear Impact Modified Acrylic Copolymer (discontinued **)
- Kazanorgsintez E-18 Petroleum Resin
- H.C. Starck Grade BF 17 Silicon Carbide, SiC
- Polyplastics Duranex® 6302T Polybutylene Terephthalate (PBT), Low friction, Low wear, Mineral filled
- A. Schulman POLYBATCH™ Silver 7002/5 Concentrate Based In LDPE
- DuPont™ Fusabond® E589 Polymer Modifier
- Elastocon TPE Technologies Elastocon® 8088N Thermoplastic Elastomer
- Arkema Group Evatane® 1005 VN 3 Ethylene Vinyl Acetate
Copyright © lookpolymers.com All Rights Reserved