- Seals Eastern 5753 Fluorocarbon-Elastomer
Seals Eastern 5753 Fluorocarbon-Elastomer
| Category | Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Seals Eastern, Inc |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Seals Eastern 5753 Fluorocarbon-Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features:MIL-SpecFKM general serviceInformation provided by Seals Eastern.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | >= 62 | >= 62 | ASTM D2240 |
| 67 | 67 | Average; ASTM D2240 | |
| Tensile Strength | >= 7.136 MPa | >= 1035 psi | ASTM D412 Method A |
| 10.58 MPa | 1534 psi | Average; ASTM D412 Method A | |
| Tensile Stress | 1.14 MPa @Strain 25.0 % |
166 psi @Strain 25.0 % |
Average; ASTM D412 Method A |
| >= 1.23 MPa @Strain 50.0 % |
>= 178 psi @Strain 50.0 % |
ASTM D412 Method A | |
| 1.72 MPa @Strain 50.0 % |
249 psi @Strain 50.0 % |
Average; ASTM D412 Method A | |
| >= 1.89 MPa @Strain 100 % |
>= 274 psi @Strain 100 % |
ASTM D412 Method A | |
| 3.00 MPa @Strain 100 % |
435 psi @Strain 100 % |
Average; ASTM D412 Method A | |
| Elongation at Break | >= 194 % | >= 194 % | ASTM D412 Method A |
| 267 % | 267 % | Average; ASTM D412 Method A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Glass Transition Temp, Tg | -20.0 °C | -4.00 °F | ASTM D1329 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Strain Energy/ Unit Volume at 20% Elongation (psi) | 18 | ASTM D412 Method A |
Users viewing this material also viewed the following:
- PolyOne Bergamid™ B700 UF V2 Polyamide 6 (Nylon 6)
- LNP Lubricomp® OFL-4536 Polyphenylene Sulfide, Glass Fiber Reinforced, PTFE Lubricant (discontinued **)
- Indium Corp. Indalloy 17 Low Melting Bismuth Alloy
- Taiwan PU Corporation TPU-CH85 High Hydrolysis Resistance, Calender Molding Polyether Base TPU
- Brandenburger S 5000 Ablation Material for Aeronautics and Space Aviation
- BASF Ultramid® HMG13 HS BK-102 63% Glass Filled PA6 (Dry)
- AIM 52In/48Sn Solder for Photonic Packaging
- BASF Ultramid® A3W PA66 (Conditioned)
- Bulk Molding Compounds BMC T12-15541 General Purpose Molding Compound
- Resinlab® EP11HT Gray Filled Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved