Seals Eastern 5725 Fluorocarbon-Elastomer
| Category | Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Seals Eastern, Inc |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Seals Eastern 5725 Fluorocarbon-Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Formulated Viton®. General service.Information provided by Seals Eastern, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 2.03 g/cc | 2.03 g/cc | ASTM D297, 15 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | >= 85 | >= 85 | ASTM D2240, Type A |
| 95 | 95 | AVG; ASTM D2240, Type A | |
| Tensile Strength at Break | >= 8.170 MPa | >= 1185 psi | ASTM D412 Method A |
| 11.98 MPa | 1737 psi | AVG; ASTM D412 Method A | |
| Tensile Strength, Yield | >= 4.46 MPa | >= 647 psi | Stress at Elongation M50; ASTM D412 Method A |
| 4.86 MPa | 705 psi | AVG Stress at Elongation M25; ASTM D412 Method A | |
| >= 5.53 MPa | >= 802 psi | Stress at Elongation M100; ASTM D412 Method A | |
| 5.83 MPa | 845 psi | AVG Stress at Elongation M50; ASTM D412 Method A | |
| 8.046 MPa | 1167 psi | AVG Stress at Elongation M100; ASTM D412 Method A | |
| Elongation at Break | >= 84 % | >= 84 % | ASTM D412 Method A |
| 200 % | 200 % | AVG; ASTM D412 Method A | |
| Modulus of Elasticity | 0.04430 GPa | 6.425 ksi | ASTM D412 Method A |
| Shear Modulus | 0.01477 GPa | 2.142 ksi | ASTM D412 Method A |
| Secant Modulus | 0.0416 GPa | 6.04 ksi | ASTM D412 Method A |
| Tear Strength Test | 300 | 300 | (psi); ASTM D624, Die B |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Glass Transition Temp, Tg | -20.0 °C | -4.00 °F | ASTM D1329 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Shelf Life | 240 Month | 240 Month | ASTM D395, Test B |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Strain Energy / Unit Volume at 20% Elongation (psi) | 98 |
Users viewing this material also viewed the following:
- NOVA Chemicals Arcel 730 LV Resin 70% Polystyrene/30% Polyethylene
- Kazanorgsintez E-10 Petroleum Resin
- Karina E 813-10/164-B-RT-PO White PVC Compound
- Schott Nextrema® 724-3 Glass Ceramic
- Goodfellow Manganese 70/Nickel 30 Alloy
- A. Schulman POLYBATCH™ U-6634-L Blowing Agent Concentrate Based In PE
- Chengdu Polyster RPM650 Flame Retardant Masterbatch
- Bulk Molding Compounds BMC 605 Mineral Filled, Glass Fiber Reinforced Polyester Compound
Copyright © lookpolymers.com All Rights Reserved