Samsung Cheil Industries Infino® HP-1000XA PC/ABS, Unreinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® HP-1000XA PC/ABS, Unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PC/ABS material for automobile IP-coreInformation provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 28 g/10 min @Load 10.0 kg, Temperature 250 °C |
28 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 113 | 113 | ASTM D785 |
| Tensile Strength, Yield | 53.9 MPa | 7820 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 100 % | 100 % | 50 mm/min; ASTM D638 |
| Flexural Strength | 73.5 MPa | 10700 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.01 GPa | 292 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 4.41 J/cm @Thickness 6.35 mm |
8.27 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C @Thickness 6.40 mm |
230 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 123 °C | 253 °F | B/50; ISO R306 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® SLX1432T PC Copolymer
- Malvern Minerals Novakup® 200 Surface-Treated Lamellar Quartz Filler/Extender
- Silberline SilBerCote® 5245-20Z
- Westlake Hifor Xtreme SC74853 Linear Low Density Polyethylene
- ExxonMobil Santoprene® 8271-55 Thermoplastic Elastomer
- DuPont Teijin Films Mylar® HR951 Polyester Film, 140 Gauge
- Arlon 930-10Bxx-P0 0.030" (0.762 mm) Cured Self-fusing Silicone Tape
- Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 11.1 mm thick plate, aged 3 hours at 816°C
Copyright © lookpolymers.com All Rights Reserved