- SABIC Innovative Plastics Valox® EH7020HF PBT+PET
SABIC Innovative Plastics Valox® EH7020HF PBT+PET
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PET + PBT Unreinforced , Polyethylene Terephthalate (PET) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® EH7020HF PBT+PET.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Valox EH7020HF is a mineral filled PBT/PET that offers good surface appearance, high flow and good heat performance. EH7020HF was developed for automotive bezel application that requires basecoat + top coat metalization. EH7020HF is higher flow version of EH7020.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.49 g/cc | 1.49 g/cc | ASTM D792 |
| Density | 1.49 g/cc | 0.0538 lb/in³ | ISO 1183 |
| Melt Flow | 36 g/10 min @Load 1.20 kg, Temperature 266 °C |
36 g/10 min @Load 2.65 lb, Temperature 511 °F |
ASTM D1238 |
| 64 g/10 min @Load 2.16 kg, Temperature 265 °C |
64 g/10 min @Load 4.76 lb, Temperature 509 °F |
ASTM D1238 | |
| Melt Index of Compound | 52 g/10 min @Load 2.16 kg, Temperature 265 °C |
52 g/10 min @Load 4.76 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0 MPa | 7980 psi | Type I, 5 mm/min; ASTM D638 |
| 57.0 MPa | 8270 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | 5 mm/min; ISO 527 |
| 56.0 MPa | 8120 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.9 % | 1.9 % | 5 mm/min; ISO 527 |
| 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 4.80 GPa | 696 ksi | 1 mm/min; ISO 527 |
| 5.88 GPa | 853 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 93.0 MPa | 13500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 96.0 MPa | 13900 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 4.68 GPa | 679 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 4.71 GPa | 683 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.270 J/cm | 0.506 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | 80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C | 171 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 70.0 °C @Thickness 3.20 mm |
158 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 179 °C | 354 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- RheTech Products HP514-394 14% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, 102E Medium Oak
- Palm Labs Adhesives Turbo Fuse Series 160SI Surface Insensitive (1000 Viscosity) Rapid Bonding Adhesive
- DuPont™ Clysar® HP Polyolefin Shrink Packaging Film, 60 Gauge (discontinued **)
- PolyOne Stat-Tech™ AS-15GF/000 SD ABS - 15% Glass Fiber Reinforced - Antistatic Protection (discontinued **)&
- Momentive Performance Materials Siloprenâ„¢ LSR 3486/35 Liquid Silicone Rubber - Self-Lubricating / Low Compression Set
- Shakespeare CL-10XT Super Tough Nylon Copolymer Fishing Line, 10 lb
- Teknor Apex MF 826 Polyvinyl Chloride, Flexible Film
- Chosun Refractories HAL-SNA Nozzle Brick
- Chosun Refractories HSC-18RA Dense and High-Strength Castable, Superdense
Copyright © lookpolymers.com All Rights Reserved