SABIC Innovative Plastics Valox® 732E PBT + PC + PET
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polyester, TP , Polybutylene Terephthalate (PBT) , Polyethylene Terephthalate (PET) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® 732E PBT + PC + PET.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% glass/mineral reinforced, excellent thermal performance, low shrinkage and warp. Easy flow.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.51 g/cc | 1.51 g/cc | ASTM D792 |
| Water Absorption | 0.070 % @Time 86400 sec |
0.070 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0040 cm/cm @Thickness 1.50 - 3.20 mm |
0.0030 - 0.0040 in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
| 0.0040 - 0.0060 cm/cm @Thickness 3.20 - 4.60 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 - 0.181 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Thickness 1.50 - 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
| 0.0060 - 0.0080 cm/cm @Thickness 3.20 - 4.60 mm |
0.0060 - 0.0080 in/in @Thickness 0.126 - 0.181 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 109 | 109 | ASTM D785 |
| Tensile Strength at Break | 82.0 MPa | 11900 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 |
| Flexural Strength | 124 MPa | 18000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 6.89 GPa | 999 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 1.01 J/cm | 1.89 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.34 J/cm | 10.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 25.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
14.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 25.2 µm/m-°C @Temperature 60.0 - 138 °C |
14.0 µin/in-°F @Temperature 140 - 280 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C @Thickness 6.40 mm |
419 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C @Thickness 6.40 mm |
388 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.32 @Frequency 1.00e+6 Hz |
3.32 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 3.53 @Frequency 50.0 - 60.0 Hz |
3.53 @Frequency 50.0 - 60.0 Hz |
ASTM D150 | |
| Dielectric Strength | 17.9 kV/mm @Thickness 3.20 mm |
455 kV/in @Thickness 0.126 in |
in oil; ASTM D149 |
| Dissipation Factor | 0.0080 @Frequency 50.0 - 60.0 Hz |
0.0080 @Frequency 50.0 - 60.0 Hz |
ASTM D150 |
| 0.013 @Frequency 1.00e+6 Hz |
0.013 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Specific Volume | 0.66cm^3/g | ASTM D792 |
Users viewing this material also viewed the following:
- LNP Thermocomp® LF-1006 EM Polyetheretherketone, Glass Fiber Reinforcement (discontinued **)
- Huntsman Kerimid 701-1 B US Resin
- Michelman® Michem® Lube 160PF Anionic carnauba wax emulsion
- Gwent Electronic Materials C1991025D2 Gold Ink
- Washington Penn PPH3TF4-BLK Polypropylene, 40% Talc Filled
- Polyplastics Duranex® 750LD Polybutylene Terephthalate (PBT), Low warpage, 30% GF filled
- China Tungsten YG8 Cemented Tungsten Carbide for Mining Purposes
- 3M Cool Roofing Granule (Corona)
- 3M FP024502 Removable White Polypropylene Label Products
Copyright © lookpolymers.com All Rights Reserved