SABIC Innovative Plastics LNP Verton OX07411 PPS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Verton OX07411 PPS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Verton* OX07411 is a compound based on Polyphenylene Sulfide resin containing Long Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in³ | ASTM D 792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 191 MPa | 27700 psi | ASTM D 638 |
| 198 MPa | 28700 psi | ISO 527 | |
| Tensile Strength, Yield | 191 MPa | 27700 psi | ASTM D 638 |
| 198 MPa | 28700 psi | ISO 527 | |
| Elongation at Break | 1.6 % | 1.6 % | ASTM D 638 |
| 1.8 % | 1.8 % | ISO 527 | |
| Elongation at Yield | 1.6 % | 1.6 % | ASTM D 638 |
| 1.8 % | 1.8 % | ISO 527 | |
| Tensile Modulus | 14.4 GPa | 2090 ksi | 1 mm/min; ISO 527 |
| 15.78 GPa | 2289 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 267 MPa | 38700 psi | ASTM D 790 |
| 285 MPa | 41300 psi | ISO 178 | |
| Flexural Modulus | 16.75 GPa | 2429 ksi | ASTM D 790 |
| 17.7 GPa | 2570 ksi | ISO 178 | |
| Izod Impact, Notched | 2.18 J/cm @Temperature 23.0 °C |
4.08 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 7.42 J/cm @Temperature 23.0 °C |
13.9 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 25.0 kJ/m² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 277 °C @Thickness 3.20 mm |
531 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 10000 - 1.00e+6 ohm-cm | 10000 - 1.00e+6 ohm-cm | ASTM D 257 |
Users viewing this material also viewed the following:
- PPT FP95 Fully Sintered Ferrite Powder
- Plenco 50015 PET, Pellet, Injection Molded, White (discontinued **)
- Polymer Resources PPX-GP2 Modified PPO, General Purpose with HDT of 250 F (Unverified Data**)
- Lehmann & Voss LUVOCOM® 80/TF/18/NT Polyacetal-copolymer, with PTFE
- A. Schulman POLYBATCH™ ASC-331 Inorganic Antislip Masterbatch Based in Polyethylene
- Fainplast Compounds PK 8025 Flexible PVC, Lead Free
- 3M Scotch® 3785 Performance Continuous Taping System Tape
- Samsung Cheil Industries Infino® UF-1017S PC, Unreinforced FR
- Techmer ES HiFill® SPS GF40 BK 40% Glass Filled
Copyright © lookpolymers.com All Rights Reserved