SABIC Innovative Plastics LNP THERMOCOMP DX06094 PC (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP THERMOCOMP
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP THERMOCOMP DX06094 PC (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* THERMOCOMP* DX06094 is a compound based on Polycarbonate resin containing Glass Fiber . Added features include: High Impact, Non- Brominated & Non-Chlorinated Flame Retardant and Mold Release. UL listing for BK only.

Physical Properties	Metric	English	Comments
Density	1.42 g/cc	0.0513 lb/inÂ³	ISO 1183
Linear Mold Shrinkage, Flow	0.0022 cm/cm	0.0022 in/in	SABIC Method

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	145 MPa	21000 psi	5 mm/min; ISO 527
Elongation at Break	3.0 %	3.0 %	5 mm/min; ISO 527
Tensile Modulus	9.00 GPa	1310 ksi	1 mm/min; ISO 527
Flexural Strength	206 MPa	29900 psi	2 mm/min; ISO 178
Flexural Yield Strength	208 MPa	30200 psi	2 mm/min; ISO 178
Flexural Modulus	8.50 GPa	1230 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	12.0 kJ/mÂ²	5.71 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	48.0 kJ/mÂ²	22.8 ft-lb/inÂ²	80104; ISO 180/1U

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	23.0 Âµm/m-Â°C @Temperature 23.0 - 60.0 Â°C	12.8 Âµin/in-Â°F @Temperature 73.4 - 140 Â°F	ISO 11359-2
CTE, linear, Transverse to Flow	69.0 Âµm/m-Â°C @Temperature 23.0 - 60.0 Â°C	38.3 Âµin/in-Â°F @Temperature 73.4 - 140 Â°F	ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi)	138 Â°C	280 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
Flammability, UL94	V-0 @Thickness 3.00 mm	V-0 @Thickness 0.118 in	UL 94