SABIC Innovative Plastics LNP Stat-kon OEL36A PPS
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Stat-kon OEL36A PPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-Kon* OEL36A is a compound based on Polyphenylene Sulfide resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.54 g/cc | 1.54 g/cc | ASTM D 792 |
| Density | 1.54 g/cc | 0.0556 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.030 % | 0.030 % | 23°C / 50% RH; ISO 62 |
| 0.020 % @Time 86400 sec |
0.020 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.00050 - 0.00070 cm/cm @Time 86400 sec |
0.00050 - 0.00070 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 168 MPa | 24400 psi | 5 mm/min; ISO 527 |
| 172 MPa | 24900 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 170 MPa | 24700 psi | Type I, 5 mm/min; ASTM D 638 |
| Elongation at Break | 0.90 % | 0.90 % | Type I, 5 mm/min; ASTM D 638 |
| 0.90 % | 0.90 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 25.16 GPa | 3649 ksi | 1 mm/min; ISO 527 |
| 26.62 GPa | 3861 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 225 MPa | 32600 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 258 MPa | 37400 psi | ISO 178 | |
| Flexural Modulus | 20.7 GPa | 3000 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 21.62 GPa | 3136 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.410 J/cm @Temperature 23.0 °C |
0.768 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 3.99 J/cm @Temperature 23.0 °C |
7.47 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 22.0 kJ/m² @Temperature 23.0 °C |
10.5 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| 5.00 J @Temperature 23.0 °C |
3.69 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 8.20 µm/m-°C @Temperature -30.0 - 30.0 °C |
4.56 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 41.3 µm/m-°C @Temperature -30.0 - 30.0 °C |
22.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 277 °C | 531 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 277 °C @Thickness 3.20 mm |
531 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 262 °C | 504 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 263 °C @Thickness 3.20 mm |
505 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.0 - 3.0 ohm | 1.0 - 3.0 ohm | ASTM D 257 |
Users viewing this material also viewed the following:
- Shell Carilon® DB6G6P30 Polyketone, Lubricated, Glass-Reinforced, Injection Molding Grade (discontinued **)&l
- Ravago Manufacturing Americas Hylon® N2017STHL Nylon 6 (DAM)
- LG Chemical XR404HJ ABS, Heat Resistance, Curl Fit
- SABIC Innovative Plastics Valox® AB9530 ABS+PBT (Asia Pacific)
- SABIC Innovative Plastics LNP THERMOCOMP WZ002 PBT
- DSM Fibre Intermediates Nyrim® 2025 (Wollastocoat®), Dry
- Arlon 99790N010 0.010" (0.254 mm) Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier
- Aclo Accutech Polypropylene Copolymer HP0334W30L Wollastonite Reinforced
- Elastocon TPE Technologies Elastocon® OF65 Thermoplastic Elastomer
- LATI LARTON K/30 30% Carbon Fiber Reinforced Polyphenylene sulfide (PPS) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved