SABIC Innovative Plastics LNP STAT-KON EE004 PEI (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON EE004 PEI (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-kon* EE004 is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00050 - 0.0025 cm/cm | 0.00050 - 0.0025 in/in | on Tensile Bar; SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 195 MPa | 28300 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.7 % | 1.7 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 15.2 GPa | 2200 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 264 MPa | 38300 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 12.3 GPa | 1780 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
5.56 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 47.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
26.1 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 217 °C | 423 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 10000 ohm | 100 - 10000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- RheTech Products FRP102-01 Polypropylene, Flame Retardant, Black
- Noltex Soarnol® DT2903 Ethylene Vinyl Alcohol Copolymer
- Chevron Phillips 7109BK Linear low density polyethylene blown film resin (discontinued **)
- LG Chemical LUMID GP2101BF PA66+GF10%, Halogen Free Flame Retardant
- SABIC Innovative Plastics Ultem ATX102R PEI+PCE
- Valley Adhesives EM-220 Low Temperature Application Glue Stick
- DuPont Performance Polymers Delrin® 300PE NC010A Acetal Homopolymer
- Chosun Refractories BCT-145 Acid-proof Castable
- Parker Chomerics SOFT-SHIELD® 4008 Low Closure Force, Foam Core EMI Gasket
Copyright © lookpolymers.com All Rights Reserved