SABIC Innovative Plastics LNP LUBRICOMP WAL34 PBT (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP WAL34 PBT (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* WAL34 is a compound based on Polybutylene Terephalate resin containing PTFE, Aramid Fiber. Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.014 cm/cm @Time 86400 sec |
0.014 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.020 cm/cm @Time 86400 sec |
0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 57.0 MPa | 8270 psi | ASTM D638 |
| Elongation at Break | 2.9 % | 2.9 % | ASTM D638 |
| Tensile Modulus | 4.48 GPa | 650 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 103 MPa | 14900 psi | ASTM D790 |
| Flexural Modulus | 4.39 GPa | 637 ksi | ASTM D790 |
| Coefficient of Friction, Dynamic | 0.080 | 0.080 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.060 | 0.060 | ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C @Thickness 3.20 mm |
356 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Polykemi AB SCANTEC PC S60R GF10 V0 Polycarbonate, Glass-Fiber Reinforced, Flame Retardant
- Quadrant Plastic Composites MultiQ® Impact Thermoplastic Panel Composite
- Overview of materials for PVC, 30% Glass Fiber Reinforced
- LyondellBasell Lupolen® 5236 HX HDPE, Impact Grade
- LyondellBasell Microthene® F FA70900 High Density Polyethylene
- LG Chemical Lutex 760 SBR Latex
- SABIC Innovative Plastics LNP LUBRICOMP DX09410H PC
- Saint-Gobain Tygon® F-4040-A Fuel and Lubricant Tubing Formulation
- A. Schulman SCHULAFLEX® SF 230 Ethylene-Based Butene Plastomer
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 1.5 PHR Sulfur
Copyright © lookpolymers.com All Rights Reserved