Radici Heraflex® E 4718 TPC-ET Thermoplastic Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Radici Group Plastics |
| Trade Name | Heraflex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Radici Heraflex® E 4718 TPC-ET Thermoplastic Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
TPC-ET Thermoplastic Elastomer. Low Modulus, Nominal Shore D/15s 43. Natural colorProcessing technology: Injection moldingInformation provided by Radici group.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | |
| Water Absorption | 0.45 % @Time 86400 sec |
0.45 % @Time 24.0 hour |
MI / 08 |
| Melt Flow | 34 g/10 min @Load 2.16 kg, Temperature 230 °C |
34 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 47 | 47 | Instantaneous; ISO 868 |
| 43 @Time 15.0 sec |
43 @Time 0.00417 hour |
ISO 868 | |
| Tensile Strength at Break | 34.0 MPa | 4930 psi | ISO 527-1/2 |
| Elongation at Break | 792 % | 792 % | ISO 527 1/2 |
| Flexural Modulus | 0.214 GPa | 31.0 ksi | ISO 178/1A |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| Tear Strength | 142 kN/m | 810 pli | ASTM D1004 |
| Abrasion | 19 | 19 | mm<sup>3</sup>; DIN 53516 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 185 °C | 365 °F | |
| Vicat Softening Point | 149 °C @Load 5.10 kg |
300 °F @Load 11.2 lb |
50°C/h |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V |
Users viewing this material also viewed the following:
- Precision Polymer Engineering N55E Nitrile Rubber
- NOVA Chemicals Dylark® 432 High-Heat Styrenic Copolymer
- Lehmann & Voss LUVOCOM® 1105-7760 PEEK, with carbon fiber, PTFE, lubricant modified, high viscosity
- Multibase Multi-Flex® 1047-0000 TPO Thermoplastic Polyolefin Elastomer
- LATI Latishield 87/28-10A G/20 PC, Steel/Glass Fiber Reinforced
- Wingate Alloys Winco HCP 60 Induction Hardened Turned, Ground and Polished, Hard Chromium Plated Shafting
- ExxonMobil Mobil Delvac 80W-140 Synthetic Gear Oil
- ChevronTexaco Regal® 100 R&O
- Fainplast Compounds FR 86/2 Flexible PVC, Insulation
Copyright © lookpolymers.com All Rights Reserved