- Quadrant EPP TIVAR® Dockguard - UHMW-PE - Black UV Stabilized UHMW-PE (ASTM Product Data Sheet)
Quadrant EPP TIVAR® Dockguard - UHMW-PE - Black UV Stabilized UHMW-PE (ASTM Product Data Sheet)
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), UHMW PE Ultra High Molecular Weight |
| Manufacturer | Quadrant Engineering Plastics Products |
| Trade Name | TIVAR® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Quadrant EPP TIVAR® Dockguard - UHMW-PE - Black UV Stabilized UHMW-PE (ASTM Product Data Sheet).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.940 g/cc | 0.940 g/cc | ASTM D792 |
| Water Absorption | <= 0.010 % | <= 0.010 % | Immersion, 24hr; ASTM D570(2) |
| Water Absorption at Saturation | <= 0.010 % | <= 0.010 % | Immersion; ASTM D570(2) |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 68 | 68 | ASTM D2240 |
| Tensile Strength | 37.9 MPa | 5500 psi | ASTM D638 |
| Elongation at Break | 250 % | 250 % | ASTM D638 |
| Tensile Modulus | 0.600 GPa | 87.0 ksi | ASTM D638 |
| Flexural Strength | 24.8 MPa | 3600 psi | ASTM D790 |
| Flexural Modulus | 0.800 GPa | 116 ksi | ASTM D790 |
| Compressive Strength | 22.8 MPa | 3300 psi | 10% Def.; ASTM D695 |
| Compressive Modulus | 0.689 GPa | 100 ksi | ASTM D695 |
| Izod Impact, Notched | NB | NB | ASTM D256 Type A |
| Coefficient of Friction, Dynamic | 0.15 | 0.15 | Dry vs. Steel; QTM55007 |
| Sand Slurry | 13 | 13 | 1018 Steel = 100; ASTM D4020 |
| Limiting Pressure Velocity | 0.0701 MPa-m/sec | 2000 psi-ft/min | 4:1 safety factor; QTM 55007 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 160 µm/m-°C @Temperature -40.0 - 149 °C |
89.0 µin/in-°F @Temperature -40.0 - 300 °F |
ASTM E831 |
| Melting Point | 127 °C | 260 °F | Crystalline, Peak; ASTM D3418 |
| Maximum Service Temperature, Air | 82.2 °C | 180 °F | Long Term |
| Deflection Temperature at 1.8 MPa (264 psi) | 46.7 °C | 116 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | 1/8 inch (Estimated Rating) |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistivity per Square | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ASTM D257 |
| Compliance Properties | Metric | English | Comments |
|---|---|---|---|
| 3A-Dairy | No | No | |
| Canada AG | No | No | |
| FDA | No | No | |
| NSF | No | No | |
| USDA | No | No | |
| USP Class VI | No | No |
| Chemical Resistance Properties | Metric | English | Comments |
|---|---|---|---|
| Acids, Strong (pH 1-3) | Limited | Limited | |
| Acids, Weak | Acceptable | Acceptable | |
| Alcohols | Acceptable | Acceptable | |
| Alkalies, Strong (pH 11-14) | Acceptable | Acceptable | |
| Alkalies, Weak | Acceptable | Acceptable | |
| Chlorinated Solvents | Acceptable | Acceptable | |
| Conductive / Static Dissipative | No | No | |
| Continuous Sunlight | Limited | Limited | |
| Hot Water / Steam | Limited | Limited | |
| Hydrocarbons - Aliphatic | Acceptable | Acceptable | |
| Hydrocarbons - Aromatic | Unacceptable | Unacceptable | |
| Inorganic Salt Solutions | Acceptable | Acceptable | |
| Ketones, Esters | Limited | Limited |
Users viewing this material also viewed the following:
- Noltex Soarnol® AT4403 Ethylene Vinyl Alcohol Copolymer
- Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 1.0 mm thick sheet
- Mar-Bal MB3000-15NY Thermoset Polyester Composite Molding Compound
- Ineos ABS Lustran® SAN DN79 SAN Grade
- Huntsman IROGRAN® A 92 E 4694 Polyester-Based TPU-Injection Extrusion Grade
- Shin-Etsu Silicones USG-103 Fluid
- Saint-Gobain Norton® Chemfilm® MR Fluoropolymer Cast Film
- A. Schulman POLYBATCH™ Cream 90059 Concentrate Based In Polyethylene
- ChevronTexaco RPM® Arctic Gear Lubricant
- Eurostar Staramide 6 80E10 PA6, Injection Molded
Copyright © lookpolymers.com All Rights Reserved