Polykemi AB SCANBLEND P AP2060 F20 PBT/ASA, Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , ASA Polymer , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + ASA Blend, Glass Fiber Reinforced |
| Manufacturer | Polykemi AB |
| Trade Name | SCANBLEND P |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB SCANBLEND P AP2060 F20 PBT/ASA, Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 |
| Filler Content | 20 % | 20 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | With Flow; ISO 2577 |
| 0.011 cm/cm | 0.011 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 48 g/10 min @Load 2.16 kg, Temperature 275 °C |
48 g/10 min @Load 4.76 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 100 MPa | <= 14500 psi | ISO/R527 |
| Elongation at Break | 8.0 % | 8.0 % | ISO/R527 |
| Elongation at Yield | 8.0 % | 8.0 % | ISO/R527 |
| Flexural Strength | <= 156 MPa | <= 22600 psi | ISO 178 |
| Flexural Modulus | 6.20 GPa @Temperature 23.0 °C |
899 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact Unnotched | 3.20 J/cm² @Temperature -30.0 °C |
15.2 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 5.20 J/cm² @Temperature 23.0 °C |
24.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.550 J/cm² @Temperature -20.0 °C |
2.62 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| 0.700 J/cm² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 195 °C @Load 5.001 kg |
383 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| 215 °C @Load 1.00 kg |
419 °F @Load 2.21 lb |
50°C/h; ISO 306 |
Users viewing this material also viewed the following:
- Lanxess Durethan® BKV 130 H2.0 901510 Copolyamide, 30% Glass Fiber
- Sharadaa Ceramics Sharada LTM 0.9 Insulating Castable
- Stir SpA SR 88 (PVC)
- SABIC Innovative Plastics LNP STAT-KON DE003P PC
- SABIC Innovative Plastics LNP THERMOCOMP QC008 PA6.10
- Covestro Apec® 1803 Polycarbonate
- ExxonMobil Escorene™ LD 706.15 Cast Ethylene Vinyl Acetate Copolymer
- Advanced Ceramics ACL 1085 (C-795) Alumina
- Beijing Evergrow Resources UHF-W600 UHMW PE Fiber
Copyright © lookpolymers.com All Rights Reserved