PolyOne Geon™ Vinyl Wire & Cable JG552NP Polyvinyl Chloride Alloy (PVC Alloy)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Wire and Cable Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Wire & Cable JG552NP Polyvinyl Chloride Alloy (PVC Alloy).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | ASTM D792 |
| Deformation | 16 % @Temperature 55.0 °C, Time 3600 sec |
16 % @Temperature 131 °F, Time 1.00 hour |
200 g; UL 1581 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 78 | 78 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 15.2 MPa | 2200 psi | Type IV, 510 mm/min; ASTM D638 |
| Elongation at Break | 350 % | 350 % | Type IV, 510 mm/min; ASTM D638 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | -48.0 °C | -54.4 °F | ASTM D746 |
| Oxygen Index | 28 % @Thickness 1.91 mm |
28 % @Thickness 0.0752 in |
ASTM D2863 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 160 - 170 °C | 320 - 338 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Agency Ratings | CSA LAG (Low Acid Gas) | |
| Change in Flexural Strength | 85% | ASTM D543; 70°C, 1.91 mm; in ASTM Oil #2, 96 hr |
| Change in Ultimate Elongation | -20% | ASTM D543; 70°C, 96 hr, in ASTM #2 Oil; 0.075 in |
| Features | Flame Retardant | |
| Forms | Pellets | |
| Generic Material | PVC Alloy | |
| Generic Name | Polyvinyl Chloride Alloy (PVC Alloy) | |
| HCL Evolution | 10% | CSA C22.2 No. 0.3 |
| Processing Method | Extrusion Coating | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Retention of Tensile Elongation | 75% | 121°C, 1.91 mm; 336 hr, UL Standard |
| Retention of Tensile Strength | 100% | 121°C, 1.91 mm; 336 hr, UL Standard |
| RoHS Compliance | RoHS Compliant | |
| Uses | Cable Jacketing | |
| Wire & Cable Applications |
Users viewing this material also viewed the following:
- Quadrant EPP Ertalon® 6 SA PA 6, extruded (ISO Data)
- Zircar Zirconia BusterF Alumina Bulk Fiber Insulation
- DuPont™ Sclairfilm® LWS-2 LMDPE Film, Laminating, 50.8 µm Thickness (discontinued **)
- Teknor Apex Flexalloy® 3500-60 Polyvinyl Chloride Elastomer
- Wellman Wellamid® GF33A099-HRBK Nylon 66, 33% Glass Fiber Reinforced, Hydrolysis Resistant
- ExxonMobil Mobil Clean 5W-20 Motor Oil
- Dow Engage® 8452 Polyolefin Elastomer
- Covestro Makroblend® KU 2-7912/4 Polycarbonate + PBT, Impact Grade
- Braskem H 604 Blow Molding Polypropylene
- Ascend Performance Materials Vydyne® 66B, 66J Nylon 66, Dry as Molded
Copyright © lookpolymers.com All Rights Reserved