PolyOne Geon™ Vinyl Flexible B5D02 Polyvinyl Chloride, Flexible (PVC, Flexible)
| Category | Polymer , Thermoplastic , Vinyl (PVC) |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Flexible B5D02 Polyvinyl Chloride, Flexible (PVC, Flexible).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.29 g/cc | 1.29 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.012 cm/cm | 0.0080 - 0.012 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 36 | 36 | 15 sec; ASTM D2240 |
| 50 | 50 | ASTM D2240 | |
| Tensile Strength at Break | 17.2 MPa | 2490 psi | 510 mm/min; ASTM D638 |
| Tensile Strength | 11.7 MPa @Strain 100 % |
1700 psi @Strain 100 % |
510 mm/min; ASTM D638 |
| Elongation at Break | 300 % | 300 % | 510 mm/min; ASTM D638 |
| Tear Strength | 84.1 kN/m | 480 pli | Die C, 510 mm/min; ASTM D624 |
| Compression Set | 60 % @Temperature 23.0 °C, Time 79200 sec |
60 % @Temperature 73.4 °F, Time 22.0 hour |
ASTM D395 |
| Clash Berg Modulus | 0.565 GPa | 81.9 ksi | ASTM D1043 |
| 0.310 GPa @Temperature -28.0 °C |
45.0 ksi @Temperature -18.4 °F |
ASTM D1043 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | -23.9 °C | -11.0 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 179 - 185 °C | 354 - 365 °F | |
| 196 - 207 °C | 385 - 405 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Forms | Pellets | |
| Generic Material | PVC, Flexible | |
| Generic Name | Polyvinyl Chloride, Flexible (PVC, Flexible) | |
| Processing Method | Extrusion | |
| Injection Molding | ||
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Furniture |
Users viewing this material also viewed the following:
- Ineos ABS Lustran® 2710, Extrusion Grade (discontinued **)
- Kingfa JH720 G15 15% Glass Fiber Reinforced PC
- Multibase C6-235 PERKADOX PD-50S Dow-Corning Class VI Elastomer
- A. Schulman POLYFORT™ FPP 2122UV-M-31 Black, Talc Filled Copolymer Polypropylene
- Hexcel® HexForce™ XLS9113 Carbon/Wire Fabric
- Dow Corning 2-3900 Antifoam Compound
- BASF 1,4-Dioxane stab
- Arlon 55142R040 0.040" (1.02 mm) Cured Silicone Rubber with Fiberglass Substrate
- Ascend Performance Materials Vydyne® R543H Natural Nylon 66, 43% Glass Reinforced, Conditioned
Copyright © lookpolymers.com All Rights Reserved