- PolyOne Edgetek® ES-10GF/000 PES (Polyethersulfone), 10% Glass Reinforced, Hi-Temp (discontinued **)
PolyOne Edgetek® ES-10GF/000 PES (Polyethersulfone), 10% Glass Reinforced, Hi-Temp (discontinued **)
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) , Polyethersulfone (PES), 10%Glass Fiber Filled |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® ES-10GF/000 PES (Polyethersulfone), 10% Glass Reinforced, Hi-Temp
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne™ Corporation
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 |
| Water Absorption | 0.40 % @Thickness 3.17 mm |
0.40 % @Thickness 0.125 in |
24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0050 cm/cm | 0.0040 - 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 103 MPa | 15000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 4.0 - 5.0 % | 4.0 - 5.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 4.83 GPa | 700 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 152 MPa | 22000 psi | ASTM D790 |
| Flexural Modulus | 4.14 GPa | 600 ksi | ASTM D790 |
| Izod Impact, Notched | 0.747 J/cm | 1.40 ft-lb/in | Method A, Injection Molded, 0.125 in bars, 73°F; ASTM D648 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 400 °F | Unannealed, 0.125 in bars; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 354 - 371 °C | 670 - 700 °F | Molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Processing Method | Injection Molding |
Users viewing this material also viewed the following:
- Kareline Oy PPMS5050 Natural Fiber Reinforced Polypropylene for injection molding
- Techmer ES Luriblend® PC CF10 TL10 BK 10% Carbon Filled
- ExxonMobil Mobil Jet Oil II
- Chevron Phillips Marlex® C100 Polyethylene; Enhanced
- Chosun Refractories IJM-1 Special Castable
- Covestro Texin® 985 Urethane Thermoplastic Elastomer
- California Fine Wire Alloy 443 Precious Metal Alloy
- BASF Luranyl® KR 2451/3 Polyphenylene Ether + Styrene-Butadiene Blend
Copyright © lookpolymers.com All Rights Reserved