Plenco 7527 Phenolic, Nodular, Injection Molded (discontinued **)
| Category | Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Resole, Mineral/Flock Filled |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Plenco 7527 Phenolic, Nodular, Injection Molded
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Single-Stage Phenolic. PLENCO 07527 is a flock cotton and mineral filled resole phenolic molding compound.Information supplied by Plenco
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.610 g/cc | 0.0220 lb/in³ | Apparent density per ASTM D1895 |
| Water Absorption | 0.47 % | 0.47 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0042 cm/cm | 0.0042 in/in | ATM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell E | 62 | 62 | ASTM D785 |
| Tensile Strength, Ultimate | 51.1 MPa | 7410 psi | ASTM D638 |
| Elongation at Break | 0.80 % | 0.80 % | ASTM D638 |
| Tensile Modulus | 8.70 GPa | 1260 ksi | ASTM D638 |
| Flexural Yield Strength | 79.5 MPa | 11500 psi | ASTM D790 |
| Flexural Modulus | 8.01 GPa | 1160 ksi | ASTM D790 |
| Compressive Yield Strength | 162.4 MPa | 23550 psi | ASTM D695 |
| Izod Impact, Notched | 0.210 J/cm | 0.393 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.210 J/cm² | 0.999 ft-lb/in² | ASTM D256 |
| Impact | 170 | 170 | J/m Plenco drop ball test |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 188 °C | 370 °F | Heat resistance per ASTM D794 |
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.10 mm |
V-0 @Thickness 0.122 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 2.015e+11 ohm-cm | 2.015e+11 ohm-cm | ASTM D257 |
| Dielectric Constant | 7.8 @Frequency 1e+6 Hz |
7.8 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 8.00 kV/mm | 203 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.099 @Frequency 1e+6 Hz |
0.099 @Frequency 1e+6 Hz |
ASTM D150 |
| Arc Resistance | 190 sec | 190 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
Users viewing this material also viewed the following:
- Chevron Phillips 7109DT LLDPE Blown Film Resin, Hexene Copolymer (discontinued **)
- Overview of materials for Phenolic, Novolac, Impact Grade, Filled
- Kolon SPESIN® KP212G15V0BM G/F Reinforced & Flame Retardant PBT Compound Resin
- Gouda Vuurvast VIBRON 180 T Dense Vibrating Refractory Castable
- SSAB Tunnplat Aluzink F40A Metal-coated Mild Steel
- A. Schulman SCHULAMID® 66 GF33HS 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66
- Arlon 0.020" (0.508 mm) Flexible Heater Silicone with Fiberglass Substrate (51576R020)
Copyright © lookpolymers.com All Rights Reserved