Plastic Lumber from the Plastic Lumber Co.

Category	Polymer , Renewable/Recycled Polymer , Thermoplastic , Wood and Natural Products , Wood
Manufacturer	The Plastic Lumber Company
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Plastic Lumber from the Plastic Lumber Co..pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Plastic Lumber is a product similar to wood that is made from recycled plastic jugs. Products will never splinter, rot, crumble or need painting. Plastic Lumber has rapidly gained acceptance with governments, commercial entities and individuals where no maintenance and durability are of the utmost importance.Information provided by The Plastic Lumber Company.

Physical Properties	Metric	English	Comments
Density	0.570 g/cc	0.0206 lb/in³	ASTM D6111-97
	0.917 - 0.980 g/cc	0.0331 - 0.0354 lb/in³	ASTM D792
Water Absorption	<= 0.010 %	<= 0.010 %	ASTM D570

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	65	65
Tensile Strength at Break	10.1 - 11.7 MPa	1470 - 1700 psi
Modulus of Elasticity	0.793 GPa	115 ksi
Flexural Yield Strength	6.9003 MPa	1000.8 psi	Stress at 3% Strain; ASTM D6109-97
Compressive Yield Strength	9.2210 MPa	1337.4 psi	Stress at 3% Strain; ASTM D6108-97
Compressive Modulus	0.4713 GPa	68.36 ksi	Compressive Secant Modulus; ASTM D6108-97
Secant Modulus	0.3437 GPa	49.85 ksi	Flexural Secant Modulus; ASTM D6109-97
Izod Impact, Unnotched	1.49 J/cm	2.80 ft-lb/in

Thermal Properties	Metric	English	Comments
CTE, linear	126 µm/m-°C @Temperature 20.0 °C	70.0 µin/in-°F @Temperature 68.0 °F	ASTM D696
Melting Point	225 °C	437 °F
Flash Point	330 °C	626 °F	ASTM E138

Electrical Properties	Metric	English	Comments
Electrical Resistivity	>= 10.0 ohm-cm	>= 10.0 ohm-cm	ASTM D257

Descriptive Properties	Value	Comments
Compressive Strength	3200-3800 lb/in
Nail Withdrawal	140 lbs	6 Penny Common Bright
Screw Withdrawal	350 lbs	#10 by 1 inch

Users viewing this material also viewed the following: