Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber
Manufacturer Network Polymers
Trade Name Softflex®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Network Polymers Softflex® 2910.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Softflex® Thermoplastic Elastomer AlloyInformation provided by Network Polymers Inc.
Physical Properties Metric English Comments
Specific Gravity 1.03 g/cc
1.03 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0080 cm/cm

@Thickness 3.17 mm
 0.0080 in/in

@Thickness 0.125 in
 ASTM D955
Linear Mold Shrinkage, Transverse 0.0080 cm/cm

@Thickness 3.17 mm
 0.0080 in/in

@Thickness 0.125 in
 ASTM D955
Melt Flow 0.30 g/10 min

@Load 5.00 kg,
Temperature 200 °C
 0.30 g/10 min

@Load 11.0 lb,
Temperature 392 °F
 Procedure A Condition G; ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore A 85
85
10 second dwell; ASTM D2240
91
91
Instantaneous; ASTM D2240
Tensile Strength, Yield 11.33 MPa
1643 psi
chs 20 in/min; ASTM D412
Elongation at Break 873 %
873 %
ASTM D412
50% Modulus 0.00150 GPa
0.218 ksi
ASTM D412
100% Modulus 0.00200 GPa
0.290 ksi
ASTM D412
300% Modulus 0.00340 GPa
0.493 ksi
ASTM D412
Gardner Impact 31.6 J

@Temperature -30.0 °C
 23.3 ft-lb

@Temperature -22.0 °F
 ASTM D5420
Taber Abrasion, mg/1000 Cycles 0.2409
0.2409
H22 Wheel 1000 g load/1000 cycles; ASTM D3389
Compression Set 38.5 %
38.5 %
Method B, 22 hours at 25% deflection and 23°C; ASTM D395
95.5 %

@Temperature 70.0 °C
 95.5 %

@Temperature 158 °F
 22 hours at 25% deflection; ASTM D395, Method B,
97.9 %

@Temperature 100 °C
 97.9 %

@Temperature 212 °F
 22 hours at 25% deflection; ASTM D395, Method B,
Tensile Set 3.8 %
3.8 %