| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber |
| Manufacturer | Multibase |
| Trade Name | Multi-Flex® TPE |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-Flex® TPE A 6221 C BLK.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kratonâ„¢ G.Data provided by Multibase.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.014 cm/cm | 0.014 in/in | ASTM D955 |
| Melt Flow | 10 - 14 g/10 min | 10 - 14 g/10 min | (Condition L) ASTM D-1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 62 | 62 | 10 sec; ASTM D-2240 |
| Tensile Strength, Ultimate | >= 4.00 MPa | >= 580 psi | ASTM D412 |
| Elongation at Break | >= 703 % | >= 703 % | ASTM D412 |
| Flexural Modulus | 0.0345 GPa | 5.00 ksi | method 1, Proc.B; ASTM D-790 |
| Tear Strength | >= 22.77 kN/m | >= 129.9 pli | ASTM D624 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 66 GF 20 GB 10 HI PA66, improved strength
- NOVA Chemicals Surpass® IFs730-R Octene sMDPE Food Packaging Lid Resin
- Tra-Con Tra-Bond FDA25 Food and Drug Application Epoxy Adhesive
- DSM Stanyl® TW241F8 Nylon 46-40% Glass Reinforced, Heat Stabilized, Lubricated (Asian Grade) (Cond)
- Denka TE-30 Transparent Resin Polymer (MABS resin) ABS
- Dow Buna® SB 1502 Cold polymerized Emulsion Styrene Butadiene Rubber (E-SBR)
- ExxonMobil Escorene® LD 720.01 Specialty Film Resin
- AKG Polymers Vision PP PPH BL1004 Polypropylene Homopolymer Compound
- Solvay RHODOLINE® 670 Surfactant
Copyright © lookpolymers.com All Rights Reserved