Multibase Multi-Flamâ„¢ 205 HFRI Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Multibase |
| Trade Name | Multi-Flam™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-Flamâ„¢ 205 HFRI Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features:Flame Retardant Forms:PelletsProcessing Methods:Injection MoldingInformation provided by Multibase
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM D955 |
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 15.2 MPa | 2200 psi | ASTM D638 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Flexural Strength | 20.7 MPa | 3000 psi | ASTM D790 |
| Flexural Modulus | 1.72 GPa | 250 ksi | Method I (3 point load), Procedure B); ASTM D790 |
| Izod Impact, Notched | 2.67 J/cm | 5.00 ft-lb/in | ASTM D256 |
| Gardner Impact | 18.98 J | 14.00 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 76.1 °C | 169 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | Unannealed; ASTM D648 |
| Vicat Softening Point | 120 °C | 248 °F | ASTM D1525 |
| Flammability, UL94 | V-0 | V-0 | 0.125 in |
| V-0 | V-0 | 0.0625 in | |
| Oxygen Index | 26 % | 26 % | ASTM D2863 |
Users viewing this material also viewed the following:
- LyondellBasell DPNB Dipropylene glycol normal butyl ether
- Borealis HG385MO Polypropylene
- A. Schulman POLYFLAM™ CFP 4623 20% Calcium Filled Polypropylene
- Aclo Accuguard Polypropylene HP1362V2CSL Homopolymer Flame Retardant Copper Stabilized
- Arlon 55986R028 0.0295" Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Asahi Kasei Thermofil N3-33FG-1626 33% Glass Fiber Reinforced, Heat Stabilized
- 3M Scotch® 720 Film/Fiber Tape
- 3M Pronto™ CA-4 Instant Adhesive
- Bhansali Engineering Abstron KU-650M ABS Super Heat Resistant
Copyright © lookpolymers.com All Rights Reserved