Mapal Plastics Maplon Type 3G Polypropylene Sheet
| Category | Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Sheet/Thermoforming Grade |
| Manufacturer | Mapal Plastics |
| Trade Name | Maplon |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Mapal Plastics Maplon Type 3G Polypropylene Sheet.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Maplon type “3G†is a single layer highly polished clear sheets, with anti-blocking properties.Main advantages: High clarity and low haze, Easy to convert due to reduced blocking, High durability, Water and chemical resistance, High heat resistance, Unlimited flex life of integral hinge, Suitable to offset printing with UV or Oxidation inks and can use when food contact neededMain disadvantages: Low scratch resistance
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | |
| Thickness | 500 microns | 19.7 mil | |
| Surface Tension | >= 48 dynes/cm | >= 48 dynes/cm | After 2 months from production |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 30.0 MPa @Temperature 23.0 °C |
4350 psi @Temperature 73.4 °F |
ASTM D638 |
| Film Tensile Strength at Yield, TD | 29.0 MPa @Temperature 23.0 °C |
4210 psi @Temperature 73.4 °F |
ASTM D638 |
| Film Elongation at Break, MD | >= 600 % @Temperature 23.0 °C |
>= 600 % @Temperature 73.4 °F |
ASTM D638 |
| Film Elongation at Break, TD | >= 600 % @Temperature 23.0 °C |
>= 600 % @Temperature 73.4 °F |
ASTM D638 |
| Film Elongation at Yield, MD | 24 % @Temperature 23.0 °C |
24 % @Temperature 73.4 °F |
ASTM D638 |
| Film Elongation at Yield, TD | 23 % @Temperature 23.0 °C |
23 % @Temperature 73.4 °F |
ASTM D638 |
| Modulus of Elasticity | 0.280 GPa @Temperature 23.0 °C |
40.6 ksi @Temperature 73.4 °F |
MD/TD; ASTM D638 |
| Tear Strength | <= 130 kN/m | <= 742 pli | Mapal internal |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 136 °C | 277 °F | ASTM D1525 |
| Heat Distortion Temperature | 79.0 °C | 174 °F | ASTM D648 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 11 % | <= 11 % | Values are on 500µ thick sheets |
| Gloss | >= 110 % | >= 110 % | 60°; ASTM D523 |
| Transmission, Visible | >= 98 % | >= 98 % | Depends on thickness |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Transparent, slightly yellow in bulk |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Rigid Extrusion 87727 Polyvinyl Chloride, Rigid (PVC, Rigid)
- Process Technologies Inc Silicone-White Sanitary Gasket
- Mitsubishi Hostaphan® RN, 15 micron Nominal Thickness Universal Polyethylene Terephthalate Film
- Sylvin Technologies 8600-95 Clear PVC Extrusion Compound
- Solvay Specialty Polymers Polymist® XPP 552V Polytetrafluoroethylene (PTFE)
- SABIC Innovative Plastics LNP Lubricomp KCL34 Acetal Copoly
- A. Schulman FORMION™ FI 389 Ionomer
- TSE Industries EzNATE® SS100 Aliphatic Polyurethane Resin
- DuPont Performance Polymers Hytrel® 8238 Polyester Elastomer TPC-ET (Unverified Data**)
- Braskem LL4800N PEBDL Cast Film Extrusion Polyethylene Copolymer
Copyright © lookpolymers.com All Rights Reserved