LyondellBasell Lupolen® 5621 D HDPE
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded |
| Manufacturer | LyondellBasell |
| Trade Name | Lupolen® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Lupolen® 5621 D HDPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data was collected by ISO methods and originally provided by BASF. The Lupolen® product line is now produced by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.955 g/cc | 0.0345 lb/in³ | |
| Water Absorption | 0.010 % | 0.010 % | |
| Moisture Absorption at Equilibrium | 0.010 % | 0.010 % | |
| Melt Flow | 0.265 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.265 g/10 min @Load 4.76 lb, Temperature 374 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 9.0 % | 9.0 % | |
| Tensile Modulus | 1.20 GPa | 174 ksi | |
| Tensile Impact Strength | 120 kJ/m² | 57.1 ft-lb/in² | |
| Tensile Creep Modulus, 1 hour | 450 MPa | 65300 psi | |
| Tensile Creep Modulus, 1000 hours | 310 MPa | 45000 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 160 µm/m-°C @Temperature 20.0 °C |
88.9 µin/in-°F @Temperature 68.0 °F |
|
| Melting Point | 135 °C | 275 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 83.0 °C | 181 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 45.0 °C | 113 °F | |
| Vicat Softening Point | 79.0 °C | 174 °F | |
| Flammability, UL94 | HB @Thickness 0.400 mm |
HB @Thickness 0.0157 in |
|
| Oxygen Index | 17 % | 17 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 2.4 @Frequency 100 Hz |
2.4 @Frequency 100 Hz |
|
| 2.4 @Frequency 1e+6 Hz |
2.4 @Frequency 1e+6 Hz |
||
| Dielectric Strength | 150 kV/mm | 3810 kV/in | |
| Dissipation Factor | 0.00020 @Frequency 100 Hz |
0.00020 @Frequency 100 Hz |
|
| 0.00020 @Frequency 1e+6 Hz |
0.00020 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |
Users viewing this material also viewed the following:
- Mearthane Durethaneâ„¢ S DS-340A Solid Polyurethane Elastomer
- SABIC Innovative Plastics LNP STAT-KON AX06518 ABS (Asia Pacific)
- Teknor Apex Telcar® TL-88-N873K BLK 111 Thermoplastic Elastomer
- Tra-Con Tra-Bond 526M03 Fast Cure Epoxy Adhesive
- Arlon LW401R##-P1 0.040" (1.02 mm) Cured Self-Fusing Silicone Tape (Triangular, Unsupported)
- Chem Polymer Chemlon 225 G Nylon 6, 25% Glass Fiber Reinforced
- Teknor Apex Monprene® MP-2835E Thermoplastic Elastomer
- Eurotec® Tecolen® CP30 NL XA80 PPCP, flame retardant - halogen (RoHS compliant), heat stabilized, natural
Copyright © lookpolymers.com All Rights Reserved