Lehmann & Voss LUVOCOMÂ® 1105/CF/30/EM PEEK, with carbon fiber

Category	Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Carbon Fiber Filled
Manufacturer	Lehmann & Voss & Co.
Trade Name	LUVOCOM®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lehmann & Voss LUVOCOMÂ® 1105/CF/30/EM PEEK, with carbon fiber.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.High-strength and high-stiff parts; low coefficient of expansion.Dynamic stressed parts at high movement velocity.Chemical and hydrolysis resistance parts, non flammable.Electrically conductive, suitable for continuous discharging of statically generated electricity.Bearings, sleeves, control disks, gear wheels, pump impellers, gear parts.Information provided by Lehmann & Voss & Co.KG

Physical Properties	Metric	English	Comments
Specific Gravity	1.42 g/cc	1.42 g/cc	ISO 1183
Water Absorption	<= 0.10 %	<= 0.10 %	23Â°C/24h
Linear Mold Shrinkage	0.00050 - 0.0020 cm/cm	0.00050 - 0.0020 in/in

Mechanical Properties	Metric	English	Comments
Tensile Stress	245 MPa	35500 psi
Elongation at Yield	1.6 %	1.6 %
	2.0 %	2.0 %	flexural
Modulus of Elasticity	27.0 GPa	3920 ksi
Flexural Strength	370 MPa	53700 psi
Flexural Modulus	23.0 GPa	3340 ksi
Charpy Impact Unnotched	2.50 J/cmÂ²	11.9 ft-lb/inÂ²	flatwise; ISO 179 1fU
	2.00 J/cmÂ² @Temperature -30.0 Â°C	9.52 ft-lb/inÂ² @Temperature -22.0 Â°F	ISO 179
Charpy Impact, Notched	0.800 J/cmÂ²	3.81 ft-lb/inÂ²	ISO 179 1eA
	0.800 J/cmÂ² @Temperature -30.0 Â°C	3.81 ft-lb/inÂ² @Temperature -22.0 Â°F	ISO 179 eA
Coefficient of Friction, Dynamic	0.23	0.23
Coefficient of Friction, Static	0.18	0.18

Thermal Properties	Metric	English	Comments
CTE, linear	9.00 Âµm/m-Â°C	5.00 Âµin/in-Â°F	DIN 53752
Thermal Conductivity	0.600 W/m-K	4.16 BTU-in/hr-ftÂ²-Â°F	DIN 52612
Maximum Service Temperature, Air	250 Â°C	482 Â°F
	280 Â°C	536 Â°F	short term
Deflection Temperature at 1.8 MPa (264 psi)	260 Â°C	500 Â°F
Vicat Softening Point	325 Â°C	617 Â°F	DIN ISO 306
Flammability, UL94	V-0	V-0	not recognized by UL

Electrical Properties	Metric	English	Comments
Surface Resistance	<= 10000 ohm	<= 10000 ohm
Insulation Resistance	<= 100000 ohm	<= 100000 ohm

Processing Properties	Metric	English	Comments
Processing Temperature	390 Â°C	734 Â°F	mass temp
Nozzle Temperature	360 - 380 Â°C	680 - 716 Â°F
Zone 1	360 - 370 Â°C	680 - 698 Â°F
Zone 2	380 - 390 Â°C	716 - 734 Â°F
Zone 3	390 - 400 Â°C	734 - 752 Â°F
Mold Temperature	170 - 200 Â°C	338 - 392 Â°F
Drying Temperature	120 Â°C @Time 21600 - 28800 sec	248 Â°F @Time 6.00 - 8.00 hour	or
	150 Â°C @Time 10800 - 21600 sec	302 Â°F @Time 3.00 - 6.00 hour	Dehumidifying dryer

Descriptive Properties	Value	Comments
Color	natural color (black)