LG Chemical NBR 6260 High Acrylonitrile Polymer
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | LG Chemical |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical NBR 6260 High Acrylonitrile Polymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: NBR 6250 is a copolymer of butadiene and acrylonitrile manufactured by advanced emulsion polymerization technology of Goodyear and LG Chem. NBR 6250 is a non staining, medium mooney, and medium high acrylonitrile polymer designed to aid in processing operations such as extruding and calendaring. NBR 6250 is a low temperature polymerized polymer, and such as, retains the excellent physical and processing properties of a cold nitrile rubber. NBR 6250 is a high mooney version of NBR 6240. Applications: NBR 6260 is recommended to use in packings, shoe products, chemically blown sponge, oil field products, industrial and automotive molded parts. CAS No: 9003-18-3Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.990 g/cc | 0.990 g/cc | |
| Volatiles | 0.20 % | 0.20 % | |
| Mooney Viscosity | 60 @Temperature 100 °C |
60 @Temperature 212 °F |
ML 1+4 |
| Ash | <= 0.50 % | <= 0.50 % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 29.5 MPa @Temperature 145 °C, Time 2990 sec |
4280 psi @Temperature 293 °F, Time 0.830 hour |
cured; ASTM D412 |
| Elongation at Break | 549 % @Temperature 145 °C, Time 2990 sec |
549 % @Temperature 293 °F, Time 0.830 hour |
cured; ASTM D412 |
| 300% Modulus | 0.0138 GPa @Temperature 145 °C, Time 2990 sec |
2.01 ksi @Temperature 293 °F, Time 0.830 hour |
cured; ASTM D412 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Bound AN Content | 0.34 | |
| Color | Tan | |
| Components | HAF (IRB#7) | 40 phr, ASTM D3187 |
| NBR 6260 | 100 phr, ASTM D3187 | |
| Stearic Acid | 1 phr, ASTM D3187 | |
| Sulfur | 1.5 phr, ASTM D3187 | |
| TBBS | 0.7 phr, ASTM D3187 | |
| ZnO | 3 phr, ASTM D3187 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® CY6110 PC+ABS
- Mallard Creek Polymers ROVENE® 4009 SBR Latex
- Michelman® Michem® Lube 723 Nonionic paraffin wax emulsion
- Momentive Performance Materials Ultraglaze® 4000 Construction Sealant
- SCG Chemicals EL-Leneâ„¢ H1000P High Density Polyethylene Pipe Resin
- A. Schulman VOLOY™ 461 Glass Reinforced, Flame Retardant PBT Alloy
- DSM Akulon® K223-HM6 (BLACK) Nylon 6-30% Mineral Reinforced (European and Asian Grade) (Dry)
- BCC Products BC 7062H Epoxy Casting
- LG Chemical LI923 Extrusion ASA
Copyright © lookpolymers.com All Rights Reserved