KratonÂ® D1170 B (SIBS) Linear Triblock Copolymer

Category	Polymer , Thermoplastic , Elastomer, TPE
Manufacturer	Kraton
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	KratonÂ® D1170 B (SIBS) Linear Triblock Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Kraton D1165 P is a clear, linear triblock copolymer based on styrene and isoprene with a polystyrene content of 30%. It is supplied from North America in the physical form identified: Kraton D1165 PT - supplied as a dusted dense pelletRegion: Asia Pacific, Europe, Japan, North America, and South AmericaUses: Kraton D1165 P is used in compound formulations and as a modifier of thermoplastics. It may also find use in formulating adhesives, sealants, coatings and modified bitumensApplications: Adhesives, Sealant and Coatings; Compounding and Personal Hygiene; Impact Modification; Footwear; and Bitumen ModificationInformation provided by KratonÂ®

Physical Properties	Metric	English	Comments
Specific Gravity	0.920 g/cc	0.920 g/cc	ISO 2781
Bulk Density	0.400 g/cc	0.0145 lb/inÂ³	ASTM D 1895 method B
Volatiles	<= 0.30 %	<= 0.30 %	KM 04
Viscosity	1100 cP	1100 cP	25% Toluene Solution at 25Â°C; KM 06
Melt Flow	13 g/10 min @Load 5.00 kg, Temperature 200 Â°C	13 g/10 min @Load 11.0 lb, Temperature 392 Â°F	ISO 1133
Ash	0.40 - 0.80 %	0.40 - 0.80 %	ISO 247

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	46 @Time 10.0 sec	46 @Time 0.00278 hour	Measured on compression molded slabs; ISO 868
Tensile Strength	11.0 MPa	1600 psi	Measured on a pressed sample; ISO 37
Elongation at Break	1200 %	1200 %	Measured on a pressed sample; ISO 37
300% Modulus	0.00140 GPa	0.203 ksi	Measured on a pressed sample; ISO 37

Descriptive Properties	Value	Comments
Content	Antioxidant	0.08-0.21%, Primary antioxidant is non-staining phenolic antioxidant, KM 08
	Polystyrene	17-21%, KM 03
	Total Extractables	<1.0%, KM 05