Kraton® D1126 P (SIS) Radial Copolymer
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Kraton |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kraton® D1126 P (SIS) Radial Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Kraton D1126 P is a clear, radial copolymer based on styrene and isoprene, with a polystyrene content of 21%. In addition, it has a diblock content of 30% and high melt flow. It is supplied from North America in the physical form identified: Kraton D1126 PT - supplied as a dusted dense pelletRegion: South America, Europe, Asia Pacific, North America, and Japan Uses: Kraton D1126 P is used as an ingredient in formulating adhesives, sealants and coatings. It may also find use as a modifier of bitumen or thermoplastics and in compound formulations.Applications: Adhesives, Sealant and Coatings; Compounding and Personal Hygiene; Impact Modification; Footwear; and Bitumen ModificationInformation provided by Kraton®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Volatiles | <= 0.50 % | <= 0.50 % | KM 04 |
| Viscosity | 420 cP | 420 cP | 25% Toluene Solution at 25°C; BAM 922 |
| Melt Flow | 22 g/10 min @Load 5.00 kg, Temperature 200 °C |
22 g/10 min @Load 11.0 lb, Temperature 392 °F |
|
| Ash | 0.20 - 0.40 % | 0.20 - 0.40 % | Talc; BAM 908 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 39 @Time 10.0 sec |
39 @Time 0.00278 hour |
Typical values on polymer compression molded at 300°F; ASTM D2240 |
| Tensile Strength | 7.72 MPa | 1120 psi | Typical properties on film cast from toluene solution; ASTM D412 |
| Elongation at Break | 1400 % | 1400 % | Typical properties of film cast from toluene solution; ASTM D412 |
| 300% Modulus | 0.00248 GPa | 0.360 ksi | Typical properties on film cast from toluene solution; ASTM D412 |
| Chemical Properties | Metric | English | Comments |
|---|---|---|---|
| Diblock Content | 30 % | 30 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Content | Antioxidant | 0.15-0.3%, KM 08 |
| Polystyrene | 20-23%, KM 03 | |
| Total Extractables | <1.0%, KM 05 | |
| Styrene/Rubber Ratio | 21/79 |
Users viewing this material also viewed the following:
- MV Labs RH730 (NH4)2NaRh(NO2)6 Diammonium sodium hexanitrorhodate(III)
- EVALCA EVAL® G110 Ethylene Vinyl Alcohol Copolymer Resin (discontinued **)
- Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes
- Lanxess Durethan® DP 2131/20 W1 901317 Nylon 6, 20% Glass Fiber
- SABIC Innovative Plastics LNP LUBRICOMP RAL22S PA 66 (Asia Pacific)
- ExxonMobil 605 Mobiltherm 600 Series
- A. Schulman PP 3468-01 Polypropylene Homopolymer For High Speed Extrusion
- A. Schulman POLYBATCH™ Dark Blue Oil LL40350/4 Concentrate Based In LLDPE
- Diamond Polymers ABS 7535 Injection Molding Grade, Very High Impact
- Quantum PEI - Ultem® 30% Glass Fiber Filled
Copyright © lookpolymers.com All Rights Reserved