Ineos N02J-00 Polypropylene Impact Copolymer

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer , Polypropylene, Impact Modified; Molded/Extruded
Manufacturer	Ineos Olefins & Polymers USA
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Ineos N02J-00 Polypropylene Impact Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

This is a low melt flow rate, high impact copolymer polypropylene for sheet extrusion and thick wall injection molding applications. It offers a superior balance of stiffness and impact strength for thermoformed articles where freezer to microwave performance is required. This material meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520.ApplicationsAppliancesCompoundingConsumer productsHousewaresRigid packagingBenefitsEnhanced room temperature and low temperature impactEnhanced stiffnessInformation provided by Ineos Olefins & Polymers USA

Physical Properties	Metric	English	Comments
Melt Flow	1.9 g/10 min @Load 2.16 kg, Temperature 230 Â°C	1.9 g/10 min @Load 4.76 lb, Temperature 446 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	77	77	ASTM D785
Tensile Strength, Yield	29.04 MPa @Temperature 23.0 Â°C	4212 psi @Temperature 73.4 Â°F	ASTM D638
Elongation at Break	>= 200 %	>= 200 %	ASTM D638
Flexural Modulus	1.62 GPa @Temperature 23.0 Â°C	235 ksi @Temperature 73.4 Â°F	D790B
Izod Impact, Notched	0.897 J/cm @Temperature -20.0 Â°C	1.68 ft-lb/in @Temperature -4.00 Â°F	1/8'' notched bar; ASTM D256
	NB @Temperature 23.0 Â°C	NB @Temperature 73.4 Â°F	1/8'' notched bar; ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	116 Â°C	240 Â°F	ASTM D648

Descriptive Properties	Value	Comments
Process	Injection Molding
	Sheet Extrusion
	Thermoforming
Region	Mexico	Bamberger Polymers Distribution
	US & Canada	Bamberger Polymers Distribution