Industrial Laminates/Norplex NP510A Glass Fabric

Category Polymer , Thermoset
Manufacturer Industrial Laminates/Norplex
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Industrial Laminates/Norplex NP510A Glass Fabric.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Woven glass fabric epoxy laminate. Engineered to provide NEMA grade FR-4 properties. This material contains bromine on the epoxy resin backbone. Certifiable to MIL-I-24768/27, Type GEE-FThickness Tested: 0.062" ,0.125", & 0.500"
Physical Properties Metric English Comments
Specific Gravity 1.80 - 1.90 g/cc

@Thickness 1.57 mm
 1.80 - 1.90 g/cc

@Thickness 0.0620 in
 ASTM D792
Moisture Absorption at Equilibrium 0.10 %

@Thickness 1.57 mm
 0.10 %

@Thickness 0.0620 in
 ASTM D229
Mechanical Properties Metric English Comments
Hardness, Rockwell M 105 - 125

@Thickness 1.57 mm
 105 - 125

@Thickness 0.0620 in
 ASTM D785
Tensile Strength, Yield 221 MPa

@Thickness 1.57 mm
 32000 psi

@Thickness 0.0620 in
 CW; ASTM D638
276 MPa

@Thickness 1.57 mm
 40000 psi

@Thickness 0.0620 in
 LW; ASTM D638
Modulus of Elasticity 17.9 GPa

@Thickness 1.57 mm
 2600 ksi

@Thickness 0.0620 in
 CW; ASTM D229
20.0 GPa

@Thickness 1.57 mm
 2900 ksi

@Thickness 0.0620 in
 LW; ASTM D229
Flexural Strength 359 MPa

@Thickness 1.57 mm
 52000 psi

@Thickness 0.0620 in
 CW; ASTM D790
448 MPa

@Thickness 1.57 mm
 65000 psi

@Thickness 0.0620 in
 LW; ASTM D790
Compressive Strength 455 MPa

@Thickness 12.7 mm
 66000 psi

@Thickness 0.500 in
 ASTM D695
Shear Strength 148 MPa

@Thickness 15.7 mm
 21500 psi

@Thickness 0.620 in
 ASTM D732
Izod Impact, Unnotched 3.90 J/cm

@Thickness 12.7 mm
 7.30 ft-lb/in

@Thickness 0.500 in
 CW, Cond E-48/50; ASTM D256
4.22 J/cm

@Thickness 12.7 mm
 7.90 ft-lb/in

@Thickness 0.500 in
 LW, Cond E-48/50; ASTM D256
Thermal Properties Metric English Comments
CTE, linear 10.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 5.56 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
CTE, linear, Transverse to Flow 13.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 7.22 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
Maximum Service Temperature, Air 140 °C
284 °F
Glass Transition Temp, Tg 130 °C
266 °F
Tg
Flammability, UL94 V-0

@Thickness 1.57 mm
 V-0

@Thickness 0.0620 in
Electrical Properties Metric English Comments
Dielectric Constant 4.8

@Thickness 1.57 mm
 4.8

@Thickness 0.0620 in
 Permittivity, Cond D-24/23; ASTM D150
Dielectric Strength 29.5 kV/mm

@Thickness 1.57 mm
 750 kV/in

@Thickness 0.0620 in
 Cond D-48/50; ASTM D229 S.T.
31.5 kV/mm

@Thickness 1.57 mm
 800 kV/in

@Thickness 0.0620 in
 Cond A; ASTM D229 S.T.
Dielectric Breakdown 65000 V

@Thickness 1.57 mm
 65000 V

@Thickness 0.0620 in
 Cond D-48/50; ASTM D229 S/S
66000 V

@Thickness 1.57 mm
 66000 V

@Thickness 0.0620 in
 Cond A; ASTM D229 S/S
Dissipation Factor 0.032

@Thickness 1.57 mm
 0.032

@Thickness 0.0620 in
 Cond D-24/23; ASTM D150
Arc Resistance 130 sec

@Thickness 3.17 mm
 130 sec

@Thickness 0.125 in
 ASTM D495
Comparative Tracking Index 300 V

@Thickness 3.17 mm
 300 V

@Thickness 0.125 in
 ASTM D3638
Descriptive Properties Value Comments
Bond Strength 2300 lb
0.5", ASTM D229
Color Natural, Black