- Imerys DB-Floatâ„¢ Kaolin
Imerys DB-Floatâ„¢ Kaolin
| Category | Ceramic , Clay , Kaolin Clay , Oxide , Aluminum Oxide , Silicon Oxide |
| Manufacturer | Imerys (Kentucky-Tennessee Clay Co.) |
| Trade Name | DB-Float™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Imerys DB-Floatâ„¢ Kaolin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Imerys
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 2.60 g/cc | 2.60 g/cc | |
| Brightness | 80 % | 80 % | G.E. Brightness |
| Particle Size | 0.50 µm | 0.50 µm | 27% finer than |
| 1.0 µm | 1.0 µm | 46.5% finer than | |
| 2.0 µm | 2.0 µm | 60% finer than | |
| 5.0 µm | 5.0 µm | 81.5% finer than | |
| 10 µm | 10 µm | 93.5% finer than | |
| 20 µm | 20 µm | 99% finer than | |
| Particle Mesh Size | 325 Mesh | 325 Mesh | 0.5% retained |
| pH | 4.5 - 6.5 | 4.5 - 6.5 |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 39.2 % | 39.2 % | |
| CaO | 0.040 % | 0.040 % | |
| Fe2O3 | 0.50 % | 0.50 % | |
| K2O | 0.13 % | 0.13 % | |
| Loss on Ignition(%) | 13.6 % | 13.6 % | |
| MgO | 0.040 % | 0.040 % | |
| Na2O | 0.090 % | 0.090 % | |
| SiO2 | 45.5 % | 45.5 % | |
| TiO2 | 1.66 % | 1.66 % |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP LUBRICOMP DFL28EG PC (Asia Pacific)
- KKPC KOSYN KNB 25SH Acrylonitrile Butadiene Rubber (NBR)
- Polyram RamShine PV507 ABS, Flame Retardant
- A. Schulman POLYFORT™ FPP 2496 Injection Molding Grade, Mineral Fortified Polypropylene
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 4 PHR Varox DBPH-50
- Fainplast Compounds GSK 0637/AL Flexible PVC, Injection Molding, Lead Free
- ATI Wah Chang 425™ Titanium Alloy, Solution Treated Annealed Bar 0.5 - 1.23 in. dia
- Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 760°C (1400°F)
Copyright © lookpolymers.com All Rights Reserved