Honeywell ACLAR® 11A(0.60 mil) CTFE Homopolymer, Barrier Film (discontinued **)
| Category | Polymer , Film , Thermoplastic , Fluoropolymer , Polychlorotrifluoroethylene (PCTFE); Molded |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Honeywell ACLAR® 11A(0.60 mil) CTFE Homopolymer, Barrier Film
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: ACLAR® 11A is a CTFE homopolymer, high performance barrier film for industrial and electronics applications.Information provided by Honeywell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 2.11 g/cc | 2.11 g/cc | ASTM D1505 |
| Density | 2.10 g/cc | 0.0760 lb/in³ | Yield Density |
| Water Vapor Transmission | 0.420 g/m²/day | 0.0270 g/100 in²/day | 100°F (37.8°C) / 100%RH; ASTM F1249 |
| Thickness | 15.2 microns | 0.600 mil |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 70 - 130 % | 70 - 130 % | ASTM D882 |
| Film Elongation at Break, TD | 200 - 300 % | 200 - 300 % | ASTM D882 |
| Secant Modulus, MD | 1.207 - 1.551 GPa | 175.1 - 225.0 ksi | ASTM D882 |
| Secant Modulus, TD | 1.172 - 1.413 GPa | 170.0 - 204.9 ksi | ASTM D882 |
| Tear Strength Test | 275 - 325 | 275 - 325 | graves tear TD, grams/mil; ASTM D1004 |
| 350 - 400 | 350 - 400 | graves tear MD, grams/mil; ASTM D1004 | |
| Film Tensile Strength at Break, MD | 82.7 - 138 MPa | 12000 - 20000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 41.4 - 62.1 MPa | 6000 - 9000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.209 W/m-K | 1.45 BTU-in/hr-ft²-°F | |
| Melting Point | 211 °C | 412 °F | crystalline melting point; ASTM D4591 |
| Oxygen Index | 100 % | 100 % | ASTM D2863 |
| Shrinkage, MD | 8.0 - 15 % | 8.0 - 15 % | 300°F / 149°C - 10 min.; ASTM D1204 |
| Shrinkage, TD | -13.0 - -8.00 % | -13.0 - -8.00 % | 300°F / 149°C - 10 min.; ASTM D1204 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 1.0 % | <= 1.0 % | ASTM D1003 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Flammability | non flammable |
Users viewing this material also viewed the following:
- RheTech Products RCC120-01 20% Calcium Carbonate Reinforced Polypropylene, Black, Recycled Content
- Park Electrochemical Nelco® NX9250 PTFE Laminate, Woven-Glass Reinforced
- Fibre Glast 180 Clear Gel Coat
- Haynes 214® alloy, 10% cold reduction, 980°C (1800°F) for 5 minutes
- Spartech PP7130 Talc Filled High Impact Copolymer
- Shinkong Synthetic Fibers Shinite® T101G36 PET, 36% Glass Filled
- A. Schulman POLYBATCH™ Yellow P20199/2 Concentrate Based In Copolymer PP
- Eurofoam Porocell POR 304 CM-KPA 45 EPDM Foam
- Carmel Olefins CAPILENE® SR 50 Polypropylene Impact Copolymer
- ATI Allvac® 520 Nickel Superalloy, Heat Treatment: 1121°C (2050°F) + Age
Copyright © lookpolymers.com All Rights Reserved