Hexcel® HexWeb® HRH-10 - 1/2 - 2.0 Aramid Fiber/Phenolic Resin Honeycomb

Category	Other Engineering Material , Composite Core Material , Composite Fibers , Polymer , Thermoset , Aramid , Phenolic
Manufacturer	Hexcel
Trade Name	HexWeb®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Hexcel® HexWeb® HRH-10 - 1/2 - 2.0 Aramid Fiber/Phenolic Resin Honeycomb.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Designation: Material-Cell Size-Density.Hexweb HRH-10 is manufactured from NOMEX aramid fiber sheets. A thermosetting adhesive is used to bond these sheets at the nodes, and after expanding to the hexagonal or OX-Core confiation, the block is dipped in phenolic resin. After curing the resin, slices are cut to the desired thickness. For special applications, such as air directionalizing, HexWeb HRH-10 can be provided without the phenolic resin. Using this process, a wide range of cell sizes, paper thicknesses, and densities can be produced.Information provided by HexCel

Physical Properties	Metric	English	Comments
Density	0.0320 g/cc	0.00116 lb/in³

Mechanical Properties	Metric	English	Comments
Compressive Yield Strength	>= 0.621 MPa	>= 90.0 psi	Bare, min
	>= 0.655 MPa	>= 95.0 psi	Stabilized, min
	0.793 MPa	115 psi	Bare, typ
	0.827 MPa	120 psi	Stabilized, typ
Shear Modulus	0.0138 GPa	2.00 ksi	Plate Shear, W Direction, typ
	0.0310 GPa	4.50 ksi	Plate Shear, L Direction, typ
Shear Strength	>= 0.228 MPa	>= 33.0 psi	Plate Shear, W Direction, min
	0.310 MPa	45.0 psi	Plate Shear, W Direction, typ
	>= 0.621 MPa	>= 90.0 psi	Plate Shear, L Direction, min
	0.758 MPa	110 psi	Plate Shear, L Direction, typ