Hexcel® HexPly® F655 Bismaleimide Resin, Carbon Tape Form

Category Polymer , Thermoset , Polyimide, TS
Manufacturer Hexcel
Trade Name HexPly®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexPly® F655 Bismaleimide Resin, Carbon Tape Form.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Fiber: T300-12K, IM7-12KInformation provided by HexCel
Physical Properties Metric English Comments
Density 1.53 - 1.56 g/cc
0.0553 - 0.0564 lb/in³
Laminate
Volatiles <= 2.0 %
<= 2.0 %
Prepreg
Mechanical Properties Metric English Comments
Tensile Strength, Yield 16.0 MPa

@Temperature 177 °C
 2320 psi

@Temperature 351 °F
 IM7 (12K); [90°]16; Wet Condition
42.0 MPa

@Temperature 232 °C
 6090 psi

@Temperature 450 °F
 IM7 (12K); [90°]16
66.0 MPa

@Temperature 23.0 °C
 9570 psi

@Temperature 73.4 °F
148 MPa

@Temperature 177 °C
 21500 psi

@Temperature 351 °F
 T300 (6K); [+/- 45°]2s; Wet Condition
202 MPa

@Temperature 177 °C
 29300 psi

@Temperature 351 °F
 T300 (6K); [+/- 45°]2s
216 MPa

@Temperature 23.0 °C
 31300 psi

@Temperature 73.4 °F
1517 MPa

@Temperature 23.0 °C
 220000 psi

@Temperature 73.4 °F
2013 MPa

@Temperature 232 °C
 292000 psi

@Temperature 450 °F
 IM7 (12K); [0°]8
2068 MPa

@Temperature 177 °C
 299900 psi

@Temperature 351 °F
 IM7 (12K); [0°]8; Wet Condition
2730 MPa

@Temperature 23.0 °C
 396000 psi

@Temperature 73.4 °F
Elongation at Yield 0.2875 %

@Temperature 177 °C
 0.2875 %

@Temperature 351 °F
 IM7 (12K); [90°]16; Wet Condition
0.6215 %

@Temperature 232 °C
 0.6215 %

@Temperature 450 °F
 IM7 (12K); [90°]16
0.7668 %

@Temperature 23.0 °C
 0.7668 %

@Temperature 73.4 °F
1.04 %

@Temperature 23.0 °C
 1.04 %

@Temperature 73.4 °F
1.61 %

@Temperature 23.0 °C
 1.61 %

@Temperature 73.4 °F
Tensile Modulus 6.00 GPa

@Temperature 177 °C
 870 ksi

@Temperature 351 °F
 IM7 (12K); [90°]16; Wet Condition
6.50 GPa

@Temperature 177 °C
 943 ksi

@Temperature 351 °F
 T300 (6K); [+/- 45°]2s; Wet Condition
7.90 GPa

@Temperature 232 °C
 1150 ksi

@Temperature 450 °F
 IM7 (12K); [90°]16
9.20 GPa

@Temperature 23.0 °C
 1330 ksi

@Temperature 73.4 °F
15.7 GPa

@Temperature 177 °C
 2280 ksi

@Temperature 351 °F
 T300 (6K); [+/- 45°]2s
16.5 GPa

@Temperature 23.0 °C
 2390 ksi

@Temperature 73.4 °F
142.7 GPa

@Temperature 23.0 °C
 20700 ksi

@Temperature 73.4 °F
160.6 GPa

@Temperature 23.0 °C
 23290 ksi

@Temperature 73.4 °F
163.4 GPa

@Temperature 232 °C
 23700 ksi

@Temperature 450 °F
 IM7 (12K); [0°]8
164.8 GPa

@Temperature 177 °C
 23900 ksi

@Temperature 351 °F
 IM7 (12K); [0°]8; Wet Condition
Flexural Yield Strength 48.0 MPa

@Temperature 177 °C
 6960 psi

@Temperature 351 °F
 T300 (6K); [90°]16; Wet Condition
80.0 MPa

@Temperature 232 °C
 11600 psi

@Temperature 450 °F
 T300 (6K); [90°]16
107 MPa

@Temperature 177 °C
 15500 psi

@Temperature 351 °F
 T300 (6K); [90°]16
138 MPa

@Temperature 23.0 °C
 20000 psi

@Temperature 73.4 °F
1110 MPa

@Temperature 177 °C
 161000 psi

@Temperature 351 °F
 T300 (6K); [0°]16; Wet Condition
1351 MPa

@Temperature 232 °C
 195900 psi

@Temperature 450 °F
 T300 (6K); [0°]16
1655 MPa

@Temperature 177 °C
 240000 psi

@Temperature 351 °F
 T300 (6K); [0°]16
2127 MPa

@Temperature 23.0 °C
 308500 psi

@Temperature 73.4 °F
Flexural Modulus 5.30 GPa

@Temperature 177 °C
 769 ksi

@Temperature 351 °F
 T300 (6K); [90°]16; Wet Condition
7.70 GPa

@Temperature 232 °C
 1120 ksi

@Temperature 450 °F
 T300 (6K); [90°]16
9.00 GPa

@Temperature 177 °C
 1310 ksi

@Temperature 351 °F
 T300 (6K); [90°]16
9.90 GPa

@Temperature 23.0 °C
 1440 ksi

@Temperature 73.4 °F
127.6 GPa

@Temperature 177 °C
 18510 ksi

@Temperature 351 °F
 T300 (6K); [0°]16; Wet Condition
137.9 GPa

@Temperature 23.0 °C
 20000 ksi

@Temperature 73.4 °F
138.6 GPa

@Temperature 177 °C
 20100 ksi

@Temperature 351 °F
 T300 (6K); [0°]16
142.7 GPa

@Temperature 232 °C
 20700 ksi

@Temperature 450 °F
 T300 (6K); [0°]16
Compressive Yield Strength 113.3 MPa

@Temperature 177 °C
 16430 psi

@Temperature 351 °F
 T300 (6K); [0°]8; Wet Condition
164 MPa

@Temperature 23.0 °C
 23800 psi

@Temperature 73.4 °F
212 MPa

@Temperature 23.0 °C
 30700 psi

@Temperature 73.4 °F
218 MPa

@Temperature 23.0 °C
 31600 psi

@Temperature 73.4 °F
243 MPa

@Temperature 23.0 °C
 35200 psi

@Temperature 73.4 °F
243 MPa

@Temperature 177 °C
 35200 psi

@Temperature 351 °F
 IM7 (12K); Open Hole Compression; [45°, 0°, -45°, 90°]4s; Wet Condition
285 MPa

@Temperature 232 °C
 41300 psi

@Temperature 450 °F
 IM7 (12K); Open Hole Compression; [45°, 0°, -45°, 90°]4s
336 MPa

@Temperature 23.0 °C
 48700 psi

@Temperature 73.4 °F
968 MPa

@Temperature 177 °C
 140000 psi

@Temperature 351 °F
 IM7 (12K); [0°]8; Wet Condition
1181 MPa

@Temperature 232 °C
 171300 psi

@Temperature 450 °F
 IM7 (12K); [0°]8
1575 MPa

@Temperature 177 °C
 228400 psi

@Temperature 351 °F
 T300 (6K); [0°]8
1671 MPa

@Temperature 23.0 °C
 242400 psi

@Temperature 73.4 °F
2167 MPa

@Temperature 23.0 °C
 314300 psi

@Temperature 73.4 °F
Compressive Modulus 38.9 GPa

@Temperature 23.0 °C
 5640 ksi

@Temperature 73.4 °F
42.6 GPa

@Temperature 23.0 °C
 6180 ksi

@Temperature 73.4 °F
51.7 GPa

@Temperature 23.0 °C
 7500 ksi

@Temperature 73.4 °F
51.7 GPa

@Temperature 23.0 °C
 7500 ksi

@Temperature 73.4 °F
Shear Modulus 2.80 GPa

@Temperature 177 °C
 406 ksi

@Temperature 351 °F
 IM7 (12K); [+/- 45°]2s; Wet Condition
3.90 GPa

@Temperature 232 °C
 566 ksi

@Temperature 450 °F
 IM7 (12K); [+/- 45°]2s
4.30 GPa

@Temperature 177 °C
 624 ksi

@Temperature 351 °F
 T300 (6K); [+/- 45°]2s
4.90 GPa

@Temperature 23.0 °C
 711 ksi

@Temperature 73.4 °F
5.20 GPa

@Temperature 23.0 °C
 754 ksi

@Temperature 73.4 °F
Shear Strength 52.0 MPa
7540 psi
T300 (6K); Short Beam; [0°]16
52.0 MPa
7540 psi
T300 (6K); Short Beam; [0°]16; Wet Condition