Hexcel® HexPly® F652 Bismaleimide Resin, Carbon Fabric Form

Category Polymer , Thermoset , Polyimide, TS
Manufacturer Hexcel
Trade Name HexPly®
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Hexcel® HexPly® F652 Bismaleimide Resin, Carbon Fabric Form.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Material Description: F3G584-60; Fiber: T300-3K; T300/13.5 mils (0.343 mm) per plyInformation provided by HexCel
Physical Properties Metric English Comments
Density 1.53 - 1.55 g/cc
0.0553 - 0.0560 lb/in³
Laminate
Volatiles <= 2.0 %
<= 2.0 %
Prepreg
Mechanical Properties Metric English Comments
Tensile Strength, Yield 57.9 MPa
<br>@Temperature 23.0 °C
 8400 psi
<br>@Temperature 73.4 °F
Tensile Modulus 76.19 GPa
11050 ksi
Flexural Yield Strength 359.6 MPa
<br>@Temperature 316 °C
 52160 psi
<br>@Temperature 601 °F
 Press Cured; Tested at 316°C after 5-10 min at 316°C
621 MPa
<br>@Temperature 232 °C
 90100 psi
<br>@Temperature 450 °F
 Press Cured; Tested at 232°C after 500 hours at 232°C
674 MPa
<br>@Temperature 23.0 °C
 97800 psi
<br>@Temperature 73.4 °F
 Press Cured
Flexural Modulus 64.3 GPa
<br>@Temperature 232 °C
 9330 ksi
<br>@Temperature 450 °F
 Press Cured; Tested at 232°C after 500 hours at 232°C
66.1 GPa
<br>@Temperature 316 °C
 9590 ksi
<br>@Temperature 601 °F
 Press Cured; Tested at 316°C after 5-10 min at 316°C
72.19 GPa
<br>@Temperature 23.0 °C
 10470 ksi
<br>@Temperature 73.4 °F
 Press Cured;
Compressive Yield Strength 229 MPa
<br>@Temperature 229 °C
 33200 psi
<br>@Temperature 444 °F
 Press Cured; Tested at 316°C after 5-10 min at 316°C
324 MPa
<br>@Temperature 232 °C
 47000 psi
<br>@Temperature 450 °F
 Press Cured; Tested at 232°C after 500 hours at 232°C
478 MPa
<br>@Temperature 23.0 °C
 69300 psi
<br>@Temperature 73.4 °F
Compressive Modulus 66.3 GPa
<br>@Temperature 23.0 °C
 9620 ksi
<br>@Temperature 73.4 °F
Shear Modulus 31.7 GPa
<br>@Temperature 232 °C
 4600 ksi
<br>@Temperature 450 °F
 Short Beam; Press Cured; Tested at 232°C after 500 hours at 232°C
31.8 GPa
<br>@Temperature 316 °C
 4610 ksi
<br>@Temperature 601 °F
 Short Beam; Press Cured; Tested at 316°C after 5-10 min at 316°C
41.2 GPa
<br>@Temperature 23.0 °C
 5980 ksi
<br>@Temperature 73.4 °F
Descriptive Properties Value Comments
Cured Thickness per Ply (cm) 0.031-0.0318
Laminate
Dry Resin Content (%) 34
Prepreg
Fiber Volume (%) 64.5
Laminate