Hexcel® HexPly® F650 Bismaleimide Resin with IM6 Fiber

Category Polymer , Thermoset , Polyimide, TS
Manufacturer Hexcel
Trade Name HexPly®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexPly® F650 Bismaleimide Resin with IM6 Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Composition: IM6 Fiber, 12K, G sizes, UD Tape - 145 g/m2Information provided by HexCel
Mechanical Properties Metric English Comments
Tensile Strength, Yield 112 MPa

@Temperature 177 °C
 16200 psi

@Temperature 351 °F
 [+/-45°]; Resin Content=27%, Fiber Volume=66%; Wet condition-96 hours in boiling H2O
138 MPa

@Temperature 177 °C
 20000 psi

@Temperature 351 °F
 [+/-45°]; Resin Content=27%, Fiber Volume=66%
145 MPa

@Temperature 23.0 °C
 21000 psi

@Temperature 73.4 °F
 [+/-45°]; Resin Content=27%, Fiber Volume=66%
2774 MPa

@Temperature 23.0 °C
 402300 psi

@Temperature 73.4 °F
 [0°]; Resin Content=26%, Fiber Volume=67%
Elongation at Yield 1.66 %

@Temperature 23.0 °C
 1.66 %

@Temperature 73.4 °F
 [0°]; Resin Content=26%, Fiber Volume=67%
Tensile Modulus 9.79 GPa

@Temperature 177 °C
 1420 ksi

@Temperature 351 °F
 [+/-45°]; Resin Content=27%, Fiber Volume=66%; Wet condition-96 hours in boiling H2O
15.8 GPa

@Temperature 177 °C
 2290 ksi

@Temperature 351 °F
 [+/-45°]; Resin Content=27%, Fiber Volume=66%
19.7 GPa

@Temperature 23.0 °C
 2860 ksi

@Temperature 73.4 °F
 [+/-45°]; Resin Content=27%, Fiber Volume=66%
165 GPa

@Temperature 23.0 °C
 23900 ksi

@Temperature 73.4 °F
 [0°]; Resin Content=26%, Fiber Volume=67%
Compressive Yield Strength 917 MPa

@Temperature 177 °C
 133000 psi

@Temperature 351 °F
 [0°]; Resin Content=29%, Fiber Volume=64%; Wet condition-96 hours in boiling H2O
1089 MPa

@Temperature 232 °C
 157900 psi

@Temperature 450 °F
 [0°]; Resin Content=29%, Fiber Volume=64%
1303 MPa

@Temperature 177 °C
 189000 psi

@Temperature 351 °F
 [0°]; Resin Content=29%, Fiber Volume=64%
1862 MPa

@Temperature 23.0 °C
 270100 psi

@Temperature 73.4 °F
 [0°]; Resin Content=29%, Fiber Volume=64%
Compressive Modulus 131 GPa

@Temperature 177 °C
 19000 ksi

@Temperature 351 °F
 [0°]; Resin Content=29%, Fiber Volume=64%; Wet condition-96 hours in boiling H2O
137 GPa

@Temperature 177 °C
 19900 ksi

@Temperature 351 °F
 [0°]; Resin Content=29%, Fiber Volume=64%
139 GPa

@Temperature 232 °C
 20200 ksi

@Temperature 450 °F
 [0°]; Resin Content=29%, Fiber Volume=64%
145 GPa

@Temperature 23.0 °C
 21000 ksi

@Temperature 73.4 °F
 [0°]; Resin Content=29%, Fiber Volume=64%
Shear Strength 27.0 MPa

@Temperature 232 °C
 3920 psi

@Temperature 450 °F
 Short Beam; [0°]; Resin Content=29%, Fiber Volume=64%; Wet condition-96 hours in boiling H2O
45.0 MPa

@Temperature 177 °C
 6530 psi

@Temperature 351 °F
 Short Beam; [0°]; Resin Content=29%, Fiber Volume=64%; Wet condition-96 hours in boiling H2O
65.0 MPa

@Temperature 232 °C
 9430 psi

@Temperature 450 °F
 Short Beam; [0°]; Resin Content=29%, Fiber Volume=64%
88.9 MPa

@Temperature 177 °C
 12900 psi

@Temperature 351 °F
 Short Beam; [0°]; Resin Content=29%, Fiber Volume=64%
118 MPa

@Temperature 23.0 °C
 17100 psi

@Temperature 73.4 °F
 Short Beam; [0°]; Resin Content=29%, Fiber Volume=64%
Descriptive Properties Value Comments
Energy Release Rate (kJ/m2) 0.41