H.C. Starck Amperit® 832.6 Zirconium Oxide-Yttrium Oxide 93-7 (ZrO2-Y2O3)
| Category | Ceramic , Oxide , Zirconium Oxide |
| Manufacturer | H.C. Starck |
| Trade Name | Amperit® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | H.C. Starck Amperit® 832.6 Zirconium Oxide-Yttrium Oxide 93-7 (ZrO2-Y2O3).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.20 - 2.60 g/cc | 0.0795 - 0.0939 lb/in³ | ASTM B212 |
| Particle Size | 39 - 49 µm | 39 - 49 µm | 10% |
| 68 - 77 µm | 68 - 77 µm | 50% | |
| 107 - 125 µm | 107 - 125 µm | 90% | |
| 176 µm | 176 µm | Minimum of 99% less than |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | <= 0.10 % | <= 0.10 % | |
| Fe2O3 | <= 0.10 % | <= 0.10 % | |
| HfO2 | <= 2.5 % | <= 2.5 % | |
| SiO2 | <= 0.10 % | <= 0.10 % | |
| TiO2 | >= 0.10 % | >= 0.10 % | |
| Y2O3 | 7.0 - 9.0 % | 7.0 - 9.0 % | |
| ZrO2 | 88.1 - 93 % | 88.1 - 93 % |
Users viewing this material also viewed the following:
- DuPont Performance Polymers Delrin® 911DP BK402 Acetal Homopolymer (Unverified Data**)
- DuPont Performance Polymers Zytel® 7335F NC010 Nylon 6 (Unverified Data**)
- Henkel Hysol EA 9360 Paste Adhesive System
- A. Schulman POLYBATCH™ Cream 90059 Concentrate Based In Polyethylene
- DuPont Performance Polymers VESPEL TP-8169 Polyimide
- Asahi Kasei Leona® 13G43 43% Glass Filled Nylon 66
- Quadrant EPP Semitron® ESd 225, Extruded, Static Dissipative Acetal (ASTM Product Data Sheet)
- Lubrizol Advanced Materials PEARLBOND® 151 Linear Thermoplastic Polyurethane (discontinued **)
- Hexcel® HexWeb® CR-PAA™ 1/4-5052-0.0015 Phosphoric Acid Anodized Aluminum Honeycomb
- LATI Latilub 88/10-10T Y/10 PEEK, 10% Aramid Fiber Reinforced, PTFE Filled
Copyright © lookpolymers.com All Rights Reserved