Glastic GLASTHERM HT200 Insulation Sheet
| Category | Polymer , Thermoset , Composite SMC , Filled/Reinforced Thermoset , Polyester, TS |
| Manufacturer | Glastic |
| Trade Name | GLASTHERM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Glastic GLASTHERM HT200 Insulation Sheet.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
HT200 features:High Hot Compressive StrengthLow Thermal ConductivityOil and Moisture ResistantReduces Heat LossHelps Control TemperatureFaster Mold StartupDesigned for reducing heat losses from plastic and zinc die cast molds with operating temperatures up to 550º F. Its thermal insulating capability provides faster startups
and increased operating efficiency while its high strength provides long service life. It is asbestos-free and rugged to withstand mechanical abuse during installation. It is easily cut and machined with standard metal working equipment. Diamond cutting tools are recommended for long life.Information provided by Red Seal Electric.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.97 g/cc | 1.97 g/cc | ASTM D-792 |
| Water Absorption | 0.2 % | 0.2 % | % by wt.; ASTM D-570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 214 MPa | 31000 psi | ASTM D-790 |
| Compressive Strength | 117 MPa @Temperature 288 °C |
17000 psi @Temperature 550 °F |
ASTM D-695 |
| 124 MPa @Temperature 200 °C |
18000 psi @Temperature 392 °F |
ASTM D-695 | |
| 186 MPa @Temperature 150 °C |
27000 psi @Temperature 302 °F |
ASTM D-695 | |
| 338 MPa @Temperature 23.9 °C |
49000 psi @Temperature 75.0 °F |
ASTM D-695 | |
| Compressive Modulus | 12.4 GPa | 1800 ksi | ASTM D-695 |
| Izod Impact, Notched | 4.27 J/cm | 8.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 22.1 µm/m-°C @Temperature 20.0 °C |
12.3 µin/in-°F @Temperature 68.0 °F |
Across Surface; ASTM D-696 |
| 116.2 µm/m-°C @Temperature 20.0 °C |
64.56 µin/in-°F @Temperature 68.0 °F |
Across Thickness; ASTM D-696 | |
| Thermal Conductivity | 0.270 W/m-K | 1.87 BTU-in/hr-ft²-°F | ASTM C-177 |
| Maximum Service Temperature, Air | 211 °C | 412 °F | Continuous |
| 288 °C | 550 °F | ||
| Flammability, UL94 | HB @Thickness 2.40 mm |
HB @Thickness 0.0945 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 1.97 kV/mm | 50.0 kV/in | S/T in Air |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Standard Color | White or Green |
Users viewing this material also viewed the following:
- Omnia Plastica Omniamid PA 6 - Akulon 6 - at 50% RH
- Network Polymers MS 150 Styrene Methyl Methacrylate Terpolymer
- Iran Petrochemical (PCC) TPC - 522 FC Expandable Polystyrene
- Momentive Performance Materials Addisilâ„¢ 1150 M Industrial Molding Heat Cured Rubber
- Gwent Electronic Materials G2020520D1 Gold Metallo-Organic Ink
- Huntsman Tactix 556 Epoxy
- Techmer ES Electrablend® ABS SS5 5% Stainless Steel Filled
- Lubrizol Isoplast® 2540 Engineering Thermoplastic Polyurethane Resin for Medical Applications
- Diamond Polymers Softflex® SF 5596 Thermoplastic Elastomer
- DuPont Performance Polymers Sorona® FG3015G NC010 Polytrimethylene Terephthalate (PTT) (Unverified Data**
Copyright © lookpolymers.com All Rights Reserved