Freudenberg Simrit S80 Silicone Elastomer (VMQ)
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) , Silicone |
| Manufacturer | Freudenberg Simrit |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Freudenberg Simrit S80 Silicone Elastomer (VMQ).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
General Purpose; AMS 3301; A-A-59588 (ZZ-R-765) Class 2A, 2B Grade 40; Good heat resistance. Poor resistance to abrasion, tear and cut growth; low tensile strength; inferior resistance to oil, gasoline and solvents; poor resistance to alkalis and acids.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | Original Properties; ASTM D297 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 80 | 80 | Original Properties; ASTM D2240 |
| 78 @Temperature 150 °C |
78 @Temperature 302 °F |
ASTM #1 Oil Immersion for 70 hours; ASTM D2240 | |
| 83 @Temperature 225 °C |
83 @Temperature 437 °F |
Air Aging, 70 hours; ASTM D2240 | |
| Tensile Strength, Ultimate | 0.0434 MPa | 6.30 psi | Original Properties; ASTM D412 Die C |
| 0.0391 MPa @Temperature 225 °C |
5.67 psi @Temperature 437 °F |
Air Aging, 70 hours; ASTM D412 Die C | |
| 0.04474 MPa @Temperature 150 °C |
6.489 psi @Temperature 302 °F |
ASTM #1 Oil Immersion for 70 hours; ASTM D412 Die C | |
| Elongation at Break | 171 % | 171 % | Original Properties; ASTM D412 Die C |
| 131.67 % @Temperature 225 °C |
131.67 % @Temperature 437 °F |
Air Aging, 70 hours; ASTM D412 Die C | |
| 162.45 % @Temperature 150 °C |
162.45 % @Temperature 302 °F |
ASTM #1 Oil Immersion for 70 hours; ASTM D412 Die C | |
| Compression Set | 19 % @Temperature 150 °C, Time 252000 sec |
19 % @Temperature 302 °F, Time 70.0 hour |
45 max; ASTM D395 |
| 19 % @Temperature 150 °C, Time 252000 sec |
19 % @Temperature 302 °F, Time 70.0 hour |
30 max; ASTM D395 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Red | |
| Decomposition per AMS 3305 | ASTM #1 Oil Immersion for 70 hours at 302°F: none | |
| Low Temperature Brittleness | Pass, No cracks | ASTM D2137 |
| Surface Tackiness per AMS 3305 | ASTM #1 Oil Immersion for 70 hours at 302°F: none | |
| Volume Change (%), ASTM D471 | 1.2 | Water Immersion for 70 hours at 212°F |
| 1.7 | ASTM #1 Oil Immersion for 70 hours at 302°F |
Users viewing this material also viewed the following:
- MV Labs ER870 Er2(C2O4)3·xH2O Erbium oxalate hydrate
- Nilit FRIANYL A63 HH-TFGV 1530 Nylon 6.6 for injection molding, 15% PTFE lubricated, 30% glass fiber reinforced
- Noltex Soarnol® BG3522 Ethylene Vinyl Alcohol Copolymer
- Honeywell Capran® Oxyshield™ OBS Monoaxially Oriented, Co-Extruded Nylon 6/EVOH/Nylon 6 Clear Film
- Styron EMERGEâ„¢ 4330-15 Polycarbonate
- Dow Corning SYL-OFF® PMCP7016 Crosslinker
- Fainplast Compounds PHA 91 Flexible PVC, Transparent Extrusion
- Ineos ABS Lustran® 452 (discontinued **)
Copyright © lookpolymers.com All Rights Reserved