ExxonMobil Santoprene® 121-70M350 Thermoplastic Vulcanizate - UV Resistant

Category	Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Vulcanizate Elastomer (TPV)
Manufacturer	Exxon Chemical
Trade Name	Santoprene®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Santoprene® 121-70M350 Thermoplastic Vulcanizate - UV Resistant.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: A soft, black, UV resistant thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material is designed for gap filler applications requiring scratch resistance and good appearance. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding. It is polyolefin based and completely recyclable.Key Features:Designed for fast, easy injection molding, especially for complex part geometries.Used in sealing applications.Recommended for applications requiring superior part surface appearance.Designed to be injected at lower molding temperatures or at lower injection pressures.EU and China RoHS compliant.Processing Method: Injection Molding and Multi Injection MoldingAvailability: Africa & Middle East, Europe, North America, Asia Pacific, Latin America and South AmericaInformation provided by ExxonMobil Chemical.

Physical Properties	Metric	English	Comments
Specific Gravity	0.930 g/cc	0.930 g/cc	ASTM D792 and ISO 1183

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	70 @Time 15.0 sec	70 @Time 0.00417 hour	2 mm; ISO 868
Tensile Strength at Break	6.20 MPa	899 psi	Across Flow; ASTM D412 and ISO 37
Tensile Stress	2.60 MPa @Strain 100 %	377 psi @Strain 100 %	Across Flow; ASTM D412 and ISO 37
Elongation at Break	480 %	480 %	Across Flow; ASTM D412 and ISO 37
Compression Set	40 % @Temperature 70.0 °C, Time 79200 sec	40 % @Temperature 158 °F, Time 22.0 hour	ASTM D395B Type 1 and ISO 188 Type A