ExxonMobil Label-Lyte™ 440LL-201 OPP Film
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Label-Lyte™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Label-Lyte™ 440LL-201 OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: A matte finish, clear, one-side treated, polypropylene film intended for use as an overlaminate in pressure-sensitive labeling applications. It presents an appealing paper-like, matte appearance while providing the benefits of a typical film overlaminate, including protected print, crisp graphics, and moisture resistance. The treated, clear layer offers good adhesive bond strength.Availability: Latin America, North America and South AmericaKey Features: Matte finish Good adhesive bond strengthExcellent moisture resistance Applications: Dairy ProductsDry Foods and Beverage PowdersUses: Pressure Sensitive LabelsProcessing Method: Outer Web Adhesive Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing and Water-based Flexographic PrintingInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Thickness | 17.8 microns | 0.700 mil | ExxonMobil Method |
| Coating Weight | 15.7 g/m² | 9.80 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 174 % | 174 % | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Film Elongation at Break, TD | 60 % | 60 % | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, MD | 110 MPa | 16000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 200 MPa | 29000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 4.0 % @Temperature 135 °C |
4.0 % @Temperature 275 °F |
ExxonMobil Method |
| Shrinkage, TD | 3.0 % @Temperature 135 °C |
3.0 % @Temperature 275 °F |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 73 % | 73 % | ExxonMobil Method |
| Gloss | 10 % | 10 % | 45°, Matte Surface; ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Wetting Tension | 0.80 receding cos theta | Treated Surface |
| Yield | 44000 in2/lb |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycolac® INP564 ABS
- MV Labs TM400 TmCl3·6H2O Thulium chloride hexahydrate
- Haynes 214® alloy, 20% cold reduction
- Solvay TECHNYL® C 216 V40 PA6, 40% glass fiber, DRY
- SABIC Innovative Plastics LNP THERMOCOMP DF0049 PC (Asia Pacific)
- Engineered Syntactic Systems HZ-40 Deep Water Syntactic Foam
- DSM Arnitel® EB463 41 Shore D, Blow Molding Grade Copolyester Elastomer (North America)
- Clariant ABS4500G10BK ABS, 10% Glass Reinforced
- DuPont Teijin Films Melinex® 339 Polyester Film, 200 Gauge
Copyright © lookpolymers.com All Rights Reserved