ExxonMobil LLDPE LL 1201XV Linear Low Density Polyethylene Resin (European Grade)

Category	Polymer , Thermoplastic , Polyethylene (PE) , LLDPE
Manufacturer	Exxon Chemical
Trade Name	LLDPE
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil LLDPE LL 1201XV Linear Low Density Polyethylene Resin (European Grade).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: LL 1201 series are LLDPE grades, offering excellent combination of stiffness and optical properties (when blended with 10-20% LDPE) Availability: Africa & Middle East, Asia Pacific and Europe Additive: Antiblock: NoSlip: NoProcessing Aid: NoThermal Stabilizer: Yes Applications: Blown FilmBread BagsFood packagingForm Fill and Seal PackagingGarment FilmGeneral PackagingIndustrial PackagingLabel FilmMultilayer Packaging FilmOverwrap FilmPackaging FilmsProduce BagsShoppersShrink FilmStand Up PouchesTrash BagsZipper BagInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Density	0.925 g/cc	0.0334 lb/in³	ExxonMobil method
Melt Flow	0.70 g/10 min @Load 2.16 kg, Temperature 190 °C	0.70 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	620 %	620 %	ASTM D882
Film Elongation at Break, TD	910 %	910 %	ASTM D882
Elmendorf Tear Strength MD	50 g	50 g	ASTM D1922
Elmendorf Tear Strength TD	450 g	450 g	ASTM D1922
Dart Drop Test	70.0 g	0.154 lb	ASTM D1709A
Film Tensile Strength at Break, MD	60.0 MPa	8700 psi	ASTM D882
Film Tensile Strength at Break, TD	42.1 MPa	6100 psi	ASTM D882
1% Secant Modulus, MD	303 MPa	44000 psi	ASTM D882
1% Secant Modulus, TD	331 MPa	48000 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	<= 253 °C	<= 487 °F	Peak Melting Point; ExxonMobil method

Optical Properties	Metric	English	Comments
Haze	12 %	12 %	ASTM D1003
Gloss	53 %	53 %	45°; ASTM D2457