ExxonMobil LDPE LD 150AC Low Density Polyethylene Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer Exxon Chemical
Trade Name LDPE
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LDPE LD 150AC Low Density Polyethylene Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: LD 150 series are LDPE grades, offering good blend mechanical properties and stiffness. Several additive packages are available according to the required surface properties.Availability: Africa & Middle East, Asia Pacific and Europe Additive: Antiblock: 450 ppmSlip: 500 ppmThermal Stabilizer: YesApplications: Agricultural Film Blend Partner Co-Extrusion FilmsCollation ShrinkForm Fill and Seal Packaging Freezer FilmLamination FilmMedium Duty Shrink Film ShoppersInformation provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.923 g/cc
0.0333 lb/in³
ExxonMobil method
Melt Flow 0.75 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.75 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Antiblock Level 450 ppm
450 ppm
Slip Level 500 ppm
500 ppm
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 370 %
370 %
ASTM D882
Film Elongation at Break, TD 570 %
570 %
ASTM D882
Elmendorf Tear Strength MD 200 g
200 g
ASTM D1922
Elmendorf Tear Strength TD 200 g
200 g
ASTM D1922
Dart Drop Test 180 g
0.397 lb
ASTM D1709A
Film Tensile Strength at Break, MD 24.1 MPa
3500 psi
ASTM D882
Film Tensile Strength at Break, TD 22.8 MPa
3300 psi
ASTM D882
1% Secant Modulus, MD 221 MPa
32000 psi
ASTM D882
1% Secant Modulus, TD 262 MPa
38000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point <= 228 °C
<= 442 °F
Peak Melting Point; ExxonMobil method
Optical Properties Metric English Comments
Haze 7.0 %
7.0 %
ASTM D1003
Gloss 64 %
64 %
45°; ASTM D2457