- ExxonMobil LD 307.76 Clear, High Impact Film Resin
ExxonMobil LD 307.76 Clear, High Impact Film Resin
| Category | Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil LD 307.76 Clear, High Impact Film Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LD 307.76 film has superior impact strength and heat sealability, used in frozen and other food packaging, and high strength bags.Information provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ExxonMobil Method |
| Vinyl Acetate Content | 5.0 % | 5.0 % | ExxonMobil Method |
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ExxonMobil Method |
| Antiblock Level | 5050 ppm | 5050 ppm | |
| Slip Level | 1500 ppm | 1500 ppm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 7.45 MPa | 1080 psi | at 2% offset; ASTM D882 |
| Film Tensile Strength at Yield, TD | 7.10 MPa | 1030 psi | at 2% offset; ASTM D882 |
| Film Elongation at Break, MD | 180 % | 180 % | ASTM D882 |
| Film Elongation at Break, TD | 590 % | 590 % | ASTM D882 |
| Film Elongation at Yield, MD | 7.1 % | 7.1 % | ASTM D882 |
| Film Elongation at Yield, TD | 5.8 % | 5.8 % | ASTM D882 |
| Elmendorf Tear Strength MD | 160 g | 160 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 90 g | 90 g | ASTM D1922 |
| Dart Drop Test | 180 g | 0.397 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 22.9 MPa | 3320 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 22.3 MPa | 3240 psi | ASTM D882 |
| 1% Secant Modulus, MD | 128 MPa | 18500 psi | ASTM D882 |
| 1% Secant Modulus, TD | 144 MPa | 20900 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 103 °C | 217 °F | Peak Melting Temperature; ExxonMobil Method |
| Crystallization Temperature | 89.0 °C | 192 °F | ExxonMobil Method |
| Vicat Softening Point | 84.4 °C | 184 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 7.4 % | 7.4 % | ASTM D1003 |
| Gloss | 70 % | 70 % | 45°; ASTM D2457 |
| Transmission, Visible | 90 % | 90 % | clear; thickness not quantified |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Thermal Stabilizer |
Users viewing this material also viewed the following:
- NIZHNEKAMSKNEFTEKHIM PE 4223T (23407) Linear Low Density Polyethylene
- Polymer Resources NY66-IM1-G13 Nylon 66, 13% Glass Reinforced, Toughened
- Albis Plastics Cellulose Acetate CA700 , Unreinforced, 29% Plasticizer (discontinued **)
- Mid-Mountain Materials SILTEX® XS-150 Silica Yarn
- H.C. Starck Amperit® 825 Zirconium Oxide-Yttrium Oxide 93-7 (ZrO2-Y2O3)
- Michelman® Michem® Guard 349 Nonionic, polyethylene dispersion
- Universal Wire Works 309L Stainless Steel Electrode
- A. Schulman POLYBATCH™ Poly White P80494PF Concentrate Based In Polypropylene
- Dow Corning SYL-OFF® 294 COATING
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR N990 Filler
Copyright © lookpolymers.com All Rights Reserved