ExxonMobil Exceed™ 3512CB Film Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Very Low Density Polyethylene (VLDPE)
Manufacturer Exxon Chemical
Trade Name Exceed™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Exceed™ 3512CB Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Exceed 3512CB resin is a hexene copolymer produced using ExxonMobil Chemicals Exxpol® Technology. Films made from 3512CB resin have outstanding cold temperature toughness, impact strength and puncture. These superior strength properties, along with excellent heat sealing and hot tack performance, make this a versatile packaging resin.Availability: Latin America, North America and South AmericaAdditive: Antiblock: NoSlip: NoProcessing Aid: NoThermal Stabilizer: YesApplications: Bag in BoxBarrier Food PackagingBlown FilmCast Film Food PackagingForm Fill and Seal PackagingLamination FilmMultilayer Packaging FilmPackaging FimsPersonal CarePremium Trash BagsStand Up PouchesInformation provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.912 g/cc
0.0329 lb/in³
ASTM D1505
Thickness 20.3 microns
0.800 mil
Melt Flow 3.5 g/10 min
3.5 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 7.52 MPa
1090 psi
at 2% offset; ASTM D882
Film Tensile Strength at Yield, TD 5.72 MPa
830 psi
at 2% offset; ASTM D882
Film Elongation at Break, MD 410 %
410 %
ASTM D882
Film Elongation at Break, TD 735 %
735 %
ASTM D882
Puncture Energy 4.64 J
3.42 ft-lb
Exxon Mobil Method
Elmendorf Tear Strength MD 120 g
120 g
ASTM D1922
Elmendorf Tear Strength TD 520 g
520 g
ASTM D1922
Elmendorf Tear Strength, MD 5.91 g/micron
150 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 25.6 g/micron
650 g/mil
ASTM D1922
Dart Drop 8.366 g/micron
212.5 g/mil
ASTM D1709
Dart Drop Test 170 g
0.375 lb
ASTM D1709
Film Tensile Strength at Break, MD 76.60 MPa
11110 psi
ASTM D882
Film Tensile Strength at Break, TD 49.2 MPa
7140 psi
ASTM D882
1% Secant Modulus, MD 80.53 MPa
11680 psi
ASTM D882
1% Secant Modulus, TD 105.6 MPa
15320 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 113 °C
235 °F
Peak Melting Temperature; ExxonMobil Method
Crystallization Temperature 99.0 °C
210 °F
ExxonMobil Method
Optical Properties Metric English Comments
Haze 1.6 %
1.6 %
ASTM D1003
Gloss 90 %
90 %
45°; ASTM D2457
Descriptive Properties Value Comments
Features Thermal Stabilizer