ExxonMobil Bicor™ 70 MB OPP Film
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Bicor™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Bicor™ 70 MB OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: Bicor 70 MB is a biaxially oriented polypropylene film for use in metalized film applications. 70 MB, when metalized, is used in adhesive and extrusion laminations to reveres-printed outer webs. Metalized 70 MB has outstanding moisture and light barrier. The proprietary broad seal range layer offers excellent hot tack, seal integrity, and lap seal range when used with a coextruder outer web.Availability: North America and South AmericaKey Features:Low MST, broad seal range, strong sealsHigh Adhesion of aluminum to filmResists crazing in extrusion lamintationsApplications:BakeryBiscuits/Cookie/CrackersCrisps and SnacksFrozen FoodIce CreamUses:HFFS Flexible PackagingPre-made Bags-Flexible Packaging VFFS Flexible PackagingProcessing Method: Inner Web Adhesive Lamination, Inner Web Extrusion Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing, Surface Print Unsupported and Water-based Flexographic PrintingInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Thickness | 17.8 microns | 0.700 mil | ExxonMobil Method |
| Coating Weight | 15.7 g/m² | 9.80 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 160 % | 160 % | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Film Elongation at Break, TD | 50 % | 50 % | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Coefficient of Friction | 0.55 | 0.55 | Treated; ExxonMobil Method |
| 0.70 | 0.70 | Untreated; ExxonMobil Method | |
| Film Tensile Strength at Break, MD | 138 MPa | 20000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 256 MPa | 37100 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 3.0 % @Temperature 135 °C |
3.0 % @Temperature 275 °F |
ExxonMobil Method |
| Shrinkage, TD | 4.0 % @Temperature 135 °C |
4.0 % @Temperature 275 °F |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 2.4 % | 2.4 % | ExxonMobil Method |
| Gloss | 86 % | 86 % | 45°, Untreated Surface; ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Crimp Seal MST | 88°C | |
| Crimp Seal Strength | 440 g/in | Untreated/Untreated, 205°F (96°C), 20 psi (0.1 MPa), 0.8 sec |
| Yield | 44000 in2/lb |
Users viewing this material also viewed the following:
- Nilit FRIANYL B63 KV40 Nylon 6 for injection molding, 40% glass ball reinforced
- BP Amoco Acclear® 8249 Random Copolymer Polypropylene, High Clarity Grade (discontinued **)
- Hexcel® HexPly® ES 84 120°C Curing Epoxy Matrix, E-glass Balanced fabric 390 g/m2
- Wanhua Chemical Wanthane® WHT-1685AB Polyester Based TPU
- DuPont Performance Polymers Hytrel® 6356 Polyester Elastomer TPC-ET (Unverified Data**)
- Chosun Refractories SB75 Bricks, Oxide Bonded SiC
- Arkema Group Orgalloy® RS 6000 Nylon 6 Alloy, Rigid Grade (Conditioned)
- Asahi Glass Fluon® PB1211 15% Glass Fiber, 5% MoS2, PTFE Filled Compound
- 3M Nextel™ 440 Industrial Ceramic Fiber